Incorporation of metal nanoparticles into wood substrate and methods
View Patent ↗Metal nanoparticles were incorporated into wood. Ionic liquids were used to expand the wood cell wall structure for nanoparticle incorporation into the cell wall structure. Nanoparticles of elemental gold or silver were found to be effective surface enhanced Raman spectroscopy (SERS) imaging contrast or sensing agents. Nanoparticles of elemental iron were found to be efficient microwave absorbers and caused localized heating for disrupting the integrity of the lignocellulosic matrix. Controls suggest that the localized heating around the iron nanoparticles reduces losses of cellulose in the form of water, volatiles and CO 2 . The ionic liquid is needed during the incorporation process at room temperature. The use of small amounts of ionic liquid combined with the absence of an ionic liquid purification step and a lower energy and water use are expected to reduce costs in an up-scaled pretreatment process.
1. An article comprising:
a wood substrate,
nanoparticles deposited in cell walls in the wood substrate, wherein the nanoparticles comprise an elemental metal or metal oxide, and
an ionic liquid in the wood, the ionic liquid being a molten salt comprised of 1 ethyl-3-methyl-imidazolium having a melting temperature less than or equal to 100° C.
2. The article of claim 1 , wherein the elemental metal or metal oxide comprises iron, tin, cobalt, titanium, niobium, tantalum, chromium, molybdenum, tungsten, nickel, copper, gold, silver, alloys thereof, mixtures thereof, or oxides thereof.
3. The article of claim 1 , wherein the elemental metal or metal oxide comprises iron.
4. An article comprising:
a wood substrate,
nanoparticles deposited in cell walls in the wood substrate, wherein the nanoparticles comprise an elemental metal or metal oxide, and
an ionic liquid in the wood, the ionic liquid being a molten salt comprised of 1 ethyl-3-methyl-imidazolium acetate having a melting temperature less than or equal to 100° C.
5. The article of claim 4 , wherein the elemental metal or metal oxide comprises iron, tin, cobalt, titanium, niobium, tantalum, chromium, molybdenum, tungsten, nickel, copper, gold, silver, alloys thereof, mixtures thereof, or oxides thereof.
6. The article of claim 4 , wherein the elemental metal or metal oxide comprises iron.
7. A method for treating a wood substrate, comprising:
exposing a wood substrate having cell walls to an ionic liquid that is a molten salt that has a melting temperature at or below a temperature of 100° C. to induce swelling in the wood,
exposing the swollen wood to an aqueous suspension of nanoparticles whereby at least some of the nanoparticles become deposited in the cell walls, wherein the nanoparticles comprise an elemental metal, and
subjecting the wood and metal nanoparticles inside the wood to microwaves.
8. The method of claim 7 , wherein the ionic liquid is molten at room temperature.
9. The method of claim 7 , wherein the elemental metal is selected from iron, cobalt, titanium, niobium, tantalum, chromium, molybdenum, tungsten, nickel, copper, gold, silver, alloys thereof, and mixtures thereof.
10. The method of claim 7 , wherein the elemental metal is iron.
11. The method of claim 7 , wherein the step of exposing the wood to an ionic liquid occurs at room temperature.
12. A method for treating a wood substrate, comprising:
exposing a wood substrate having cell walls to an ionic liquid that is a molten salt that has a melting temperature at or below a temperature of 100° C. to induce swelling in the wood, and thereafter
exposing the swollen wood to an aqueous suspension of nanoparticles whereby at least some of the nanoparticles become deposited in the cell walls, wherein the nanoparticles comprise an elemental metal and the ionic liquid comprises imidazolium, and
subjecting the wood and metal nanoparticles inside the wood to microwaves.