Method for producing mixtures of alkylphosphonous acid salts and dialkylphosphinic acid salts
View Patent ↗The invention relates to a method for producing mixtures of alkylphosphonous acid and dialkylphosphinic acid salts, characterized in that a) a phosphinic acid source (I) is reacted with olefins (II) in the presence of a catalyst A to obtain a mixture of alkylphosphonous acid (III) and dialkylphosphinic acid (IV) or salts or esters thereof, and b) the thus obtained mixture of alkylphosphonous acid (III) and dialkylphosphinic acid (IV) or the salts or esters thereof is reacted with metal compounds of Mg, Ca, Al, Sb, Sn, Ge, Ti, Fe, Zr, Zn, Ce, Bi, Sr, Mn, Li, Na, K and/or a protonated nitrogen base to obtain the corresponding mixtures of alkylphosphonous acid salt (V) and dialkylphosphinic acid salt (VI) of said metals and/or a nitrogen compound, (V) (VI), wherein Y represents Mg, Ca, AI, Sb, Sn, Ge, Ti, Fe, Zr, Zn, Ce, Bi, Sr, Mn, Li, Na; K and/or a nitrogen compound and n represents ¼, ⅓, ½, 1.
1. A process for preparing mixtures of alkylphosphonous salts and dialkylphosphinic salts, comprising the steps of:
a) reacting a phosphinic acid source (I)
with ethylene
in the presence of a catalyst A to give a mixture of alkylphosphonous acid (III) and dialkylphosphinic acid (IV) or salts or esters thereof
where R 1 , R 2 , R 3 , R 4 are each H, and A and B are each ethyl and X is H, Mg, Ca, Ba, Al, Pb, Fe, Zn, Mn, Ni, Li, Na, K, where m is ⅓, ½, 1, and the catalyst A is a free-radical initiator and
b) reacting the mixture of alkylohosphonous acid (III) and dialkylphosphinic acid (IV) or salts or esters thereof with metal compounds of Mg, Ca, Al, Sb, Sn, Ge, Ti, Fe, Zr, Zn, Ce, Bi, Sr, Mn, Li, Na, K to give the mixtures of alkylphosphonous salt (V) and dialkylphosphinic salt (VI) of these metals, or a combination thereof
where A and B are each ethyl and Y is Mg, Ca, Al, Sb, Sn, Ge, Ti, Fe, Zr, Zn, Ce, Bi, Sr, Mn, Li, Na, K, or a combination thereof and n is ¼, ⅓, ½, 1
and wherein the mixture of alkylphosphonous salt (V) and dialkylphosphinic salt (VI) comprises 3 to 30% by weight of alkylphosphonous salt (V) and 70 to 97% by weight of dialkylphosphinic salt (VI).
2. The process as claimed in claim 1 , wherein the phosphinic acid source (I) is selected from the group consisting of phosphinic acid, or the sodium, potassium, calcium, magnesium, aluminum, ammonium salt methyl, ethyl, propyl, i-propyl, butyl, t-butyl, glycol ester thereof and combinations thereof.
3. The process as claimed in claim 1 , wherein the free-radical initiator is peroxomonosulfuric acid, potassium peroxomonosulfate, peroxodisulfuric acid, potassium peroxodisulfate, sodium peroxodisulfate, ammonium peroxodisulfate, hydrogen peroxide, performic acid, peracetic acid, dibenzoyl peroxide, di-tert-butyl peroxide, dicumyl peroxide, 2,4-dichlorobenzoyl peroxide, 2,2′-azobis[2-(2-imidazolin-2-yl)propane] dihydrochloride, 2,2′-azobis[2-(2-imidazolin-2-yl)propane]disulfate dihydrate, 2,2′-azobis(2-methylpropionamidine) dihydroohloride, 2,2′-azobis[2-(2-imidazolin-2-yl)propanel], 2,2′-azobis(1-imino-1-pyrrolidino-2-ethylpropane) dihydrochloride, 4,4′-azobis(4-cyanopentanoic acid) 2,2′-azobis(2,4-dimethylvaleronitrile), azobis(isobutyronitrile), 2,2′-azobis(2-metnylbutyronitrile), dimethyl 2,2′-azobis(2-methylpropionate), 1,1′-azobis(cyclohexane-1-carbonitrile), or a combination thereof.
4. The process as claimed in claim 1 , wherein the mixture of alkylphosphonous salts and dialkylphosphinic salts comprises, based on the total weight of the mixture, 0 to 5% by weight of alkylohosphonic salts, telomeric dialkylphosphinic salts or a combination thereof.
5. A flame retardant or as an intermediate for preparation of flame retardants for thermoplastic polymers, for thermoset polymers, for clearcoats, for intumescent coatings, for wood and other cellulosic products, for production of flame-retardant polymer molding compositions, for production of flame-retardant polymer moldings and/or for rendering pure and blended polyester and cellulose fabrics flame-retardant by impregnation comprising a mixture of alkylphosphonous salts and dialkylphosphinic salts prepared in accordance with the process of claim 1 .
6. The flame retardant or intermediate as claimed in claim 5 , wherein the thermoplastic polymers are polyester, polystyrene, polyamide or a combination thereof, and the thermoset polymers are unsaturated polyester resins, epoxy resins, polyurethanes, acrylates or a combination thereof.
7. The flame retardant or intermediate as claimed in claim 5 , wherein the mixture of alkylphosphonous salts and dialkylphosphinic salts comprises 0.5 to 35% by weight of alkylphosphonous salt and 65 to 99.5% by weight of dialkylphosphinic salt.
8. A flame-retardant thermoplastic or thermoset polymer molding composition comprising 2 to 50% by weight of a mixture of alkylphosphonous salts and dialkylphosphinic salts prepared according to the process of claim 1 , based on the thermoplastic or thermoset polymer.
9. A flame-retardant thermoplastic or thermoset polymer molding, film, filament or fiber comprising 2 to 50% by weight of a mixture of alkylphosphonous salts and dialkylphosphinic salts prepared according to the process of claim 1 , based on the thermoplastic or thermoset polymer.
10. A flame-retardant thermoplastic or thermoset polymer molding, film, filament or fiber comprising 3 to 40% by weight of a mixture of alkylphosphonous salts and dialkylphosphinic salts prepared according to the process of claim 1 based on the thermoplastic or thermoset polymer.