Ambient cure water-based coatings for writable-erasable surfaces
View Patent ↗Water-based coatings having writable-erasable surfaces are provided. The coatings have many desirable attributes. For example, the coatings cure under ambient conditions, have low or no VOC emissions during and upon curing, and have reduced tendency to form ghost images, even after prolonged normal use.
1. A method comprising:
combining an isocyanate resin component and an acrylic polyol resin component with each other to form a composition, wherein the composition is in a water-based carrier, and further wherein the isocyanate resin component is 20-40% by weight of the composition, the acrylic polyol resin component is 10-20% by weight of the composition, and the isocyanate resin component and the acrylic polyol resin component are present in relative amounts with respect to each other such that the composition cures under ambient conditions to form a material having a write-erasable surface, which material has at least one characteristic selected from the group consisting of:
a Sward hardness of greater than about 25;
a Taber abrasion of less than 150 mg/thousand cycles;
an elongation at break between about 5 percent and about 400 percent;
a sag resistance between about 4 mils to about 24 mils;
a contact angle measured from a surface of the material using deionized water of less than about 150 degree; and
combination thereof,
which material is further characterized in that, when its surface is written on with a marking material comprising a colorant and a solvent, the solvent comprising one or more of water, alcohols, alkoxy alcohols, ketones, ketonic alcohols, esters, acetates, mineral spirits, or mixtures thereof, the marking material can be erased from the surface of the write-erasable material to be substantially invisible for more than 100 cycles of writing and erasing at the same position.
2. The method of claim 1 , wherein the composition has pot life in a range of about 10 minutes to about 16 hours.
3. The method of claim 1 , further comprising a step of applying the composition to a substrate.
4. The method of claim 3 , wherein the step of combining and the step of applying are performed substantially simultaneously.
5. The method of claim 3 , wherein the step of applying comprises rolling, painting, spraying or any combination thereof.
6. The method of claim 3 , further comprising a step of permitting the composition to cure so that the material having a write-erasable surface is formed.
7. The method of claim 6 , further comprising a step of writing with a marking material on the write-erasable surface.
8. The method of claim 7 , further comprising a step of erasing the marking material.
9. The method of claim 1 , wherein before the step of combining the acrylic polyol resin component and the isocyanate resin component are separately stored.
10. The method of claim 9 , wherein the acrylic polyol resin component and the isocyanate component are maintained in separate containers prior to their combination.