High discharge capacity lithium battery
View Patent ↗A lithium/iron disulfide electrochemical battery cell with a high discharge capacity. The cell has a lithium negative electrode, an iron disulfide positive electrode and a nonaqueous electrolyte. The iron disulfide of the positive electrode has a controlled average particle size range which allows the electrochemical cells to exhibit desired properties in both low and high rate applications. In various embodiments, the iron disulfide particles are wet milled, preferably utilizing a media mill or milled utilizing a non-mechanical mill such as a jet mill, which reduces the iron disulfide particles to a desired average particle size range for incorporation into the positive electrode.
1. An electrochemical battery cell comprising:
a housing;
a negative electrode comprising lithium;
a positive electrode comprising a cathode mixture including naturally occurring pyrite coated onto at least a portion of each side of a thin metal strip, wherein the natural pyrite comprises iron disulfide particles having a mean diameter of a volume distribution for the iron disulfide particles that is between 1 and 19 μm;
an electrolyte mixture, comprising at least one salt dissolved in at least one non-aqueous organic solvent, disposed within the housing;
a separator disposed between the negative electrode and the positive electrode; and
wherein the negative electrode, positive electrode, and the separator form a spiral wound cylindrical electrode assembly.
2. The cell according to claim 1 , wherein the mean diameter of the volume distribution of the iron disulfide particles is less than or equal to 17 μm.
3. The cell according to claim 1 , wherein the mean diameter of the volume distribution of the iron disulfide particles is less than or equal to 6 μm.
4. The cell according to claim 1 , wherein the mean diameter of the volume distribution of the iron disulfide particles is less than or equal to 15 μm.
5. The cell according to claim 1 , wherein the separator thickness is less than or equal to 22 μm.
6. The cell according to claim 1 , wherein the cathode mixture includes at least 92 wt. % pyrite having a purity of about 95%, at least one conductive material and at least one binder.
7. The cell according to claim 1 , wherein 80% of the volume distribution of the iron disulfide particles have a diameter between 1.5 and 15 μm.
8. The cell according to claim 1 , wherein 80% of the volume distribution of the iron disulfide particles have a diameter between 1.5 and 10 μm.
9. The cell according to claim 1 , wherein the salt comprises lithium iodide and wherein the non-aqueous organic solvent includes at least one ether selected from the group consisting of: 1,2-dimethoxyethane, 1,2-diethoxyethane, di(methoxyethyl)ether, triglyme, tetraglyme diethyl ether, 1,3-dioxolane, tetrahydrofuran, 2-methyl tetrahydrofuran and 3-methyl-2-oxazolidinone.
10. The cell according to claim 1 , wherein the non-aqueous organic solvent further comprises sulfolane.
11. The cell according to claim 10 , wherein the electrolyte mixture conductivity is greater than 6 mS/cm.
12. The cell according to claim 1 , wherein the coating on each side of the strip has a thickness between 0.0010 cm to 0.010 cm.
13. The cell according to claim 1 , wherein the separator thickness is less than or equal to 16 μm and wherein the electrolyte mixture conductivity is greater than 6 mS/cm.