Implant surface with increased hydrophilicity
View Patent ↗A method of increasing the hydrophilicity of an implant to be implanted into living bone. The method comprises the act of depositing non-toxic salt residuals on the surface of the implant by exposing the surface to a solution including the non-toxic salts. The method further comprises the act of drying the implant.
1. A method of forming an implant to be implanted into living bone, the method comprising the acts of:
roughening at least a portion of the implant surface to form a roughened surface; and
increasing the hydrophilicity of the roughened surface by depositing non-toxic sodium lactate salt residuals on the roughened surface by exposing the roughened surface to a solution including the non-toxic sodium lactate salt.
2. The method of claim 1 , wherein the implant is made of titanium or titanium alloy and the act of roughening the implant surface comprises:
removing a native oxide layer from the implant surface; and
acid etching the resulting surface.
3. The method of claim 2 , wherein the implant is a dental implant including a head portion having a non-rotational feature, a lowermost end opposing the head portion, and a threaded bottom portion for engaging bone between the head portion and the lowermost end, the native oxide being removed from a threaded bottom portion of the implant.
4. The method of claim 1 , wherein the act of roughening the implant surface creates irregularities having peak-to-valley heights not greater than about 20 microns.
5. The method of claim 1 , wherein the solution is selected from the group consisting of physiological saline solution and lactated Ringer's solution.
6. The method of claim 1 , further comprising, prior to the act of depositing non-toxic sodium lactate salt residuals, depositing discrete nanoparticles on the roughened surface by exposing the roughened surface to a solution including the nanoparticles, the nanoparticles comprising a material having a property that promotes osseointegration.
7. The method of claim 6 , wherein the nanoparticles are hydroxyapatite nanocrystals and the solution including the nanoparticles is 2-methoxyethanol solvent.
8. The method of claim 7 , wherein the hydroxyapatite nanocrystals are on the order of about 20 nanometers to about 100 nanometers.
9. The method of claim 1 , wherein a contact angle formed by a deionized water droplet on the surface of the implant ranges from about 5° to about 65°.
10. The method of claim 1 , further comprising sterilizing the implant using gamma sterilization.
11. The method of claim 1 , further comprising, prior to the act of roughening, grit blasting at least a portion of the implant surface with a grit blast media.
12. The method of claim 11 , wherein the grit blast media is a resorbable grit blast media.
13. The method of claim 12 , wherein the resorbable grit blast media includes calcium phosphate.
14. The method of claim 13 , further comprising removing residual grit blast media by exposing the grit blasted portion of the implant surface to nitric acid.
15. A method of forming an implant to be implanted into living bone, the method comprising the acts of:
roughening at least a portion of the implant surface to form a roughened surface; and
increasing the hydrophilicity of the roughened surface by depositing discrete non-toxic salt residuals on the roughened surface by exposing the roughened surface to a solution including the non-toxic salt, wherein the non-toxic salt includes sodium lactate.
16. The method of claim 15 , wherein the solution is selected from the group consisting of physiological saline solution and lactated Ringer's solution.