Shrink film for label

1. A multilayered shrink film comprising:

a core layer consisting of a glycol modified polyester, the core layer having an upper and lower surface;

an upper skin layer disposed on the upper surface of the core layer and a lower skin layer disposed on the lower surface of the core layer, the skin layers each individually comprising:

(a) about 97.5 to about 99% by weight of a resin material; and

(b) about 1 to about 2.5% by weight of an antiblocking agent;

wherein the multilayered shrink film is not biaxially oriented;

wherein a thickness ratio of the core layer to the skin layers combined is about 90:10; and

wherein the resin material consists of a single polymer selected from the group consisting of a polyester, a glycol modified polyester, and a polyolefin;

wherein the glycol modified polyesters of the core layer and of the resin material in the skin layers are derived from: (i) a dicarboxylic acid and a difunctional alcohol other than ethylene glycol; or (ii) a difunctional carboxylic acid and at least two difunctional alcohols, one of which is ethylene glycol;

and wherein the shrink film has a shrink initiation temperature of about 45 to about 65° C. in a first direction.

2. The shrink film of claim 1 , wherein the difunctional carboxylic acid is chosen from terephthalic acid, isophthalic acid, phthalic acid, 2,5-dimethylterephthalic acid, 5-t-butylisophthalic acid, 4,4′-biphenyldicarboxylic acid, trans-3,3′-stilbenedicarboxylic acid, trans-4,4′-stilbenedicarboxylic acid, 4,4′-dibenzyldicarboxylic acid, 1,4-naphthalenedicarboxylic acid, 1,5-naphthalenedicarboxylic acid, 2,3-naphthalenedicarboxylic acid, 2,6-naphthalenedicarboxylic acid, 2,7-naphthalenedicarboxylic acid, 2,2,6,6-tetramethylbiphenyl-4,4′-dicarboxylic acid, 1,1,3-trimethyl-3-phenylindene-4,5-dicarboxylic acid, 1,2-diphenoxyethane-4,4′-dicarboxylic acid, diphenyl ether dicarboxylic acid, 2,5-anthracenedicarboxylic acid, 2,5-pyridinedicarboxylic acid, or a combination of two or more thereof.

3. The shrink film of claim 1 , wherein the difunctional alcohol or at least two difunctional alcohols are chosen from aliphatic diols, alicyclic diols, aromatic diols, or combinations of two or more thereof.

4. The shrink film of claim 3 , wherein the difunctional alcohols is chosen from ethylene glycol, diethylene glycol, 1,2-propanediol, 1,3-propanediol, 1,3-butanediol, 1,4-butanediol, 1,5-pentanediol, 2,2-dimethyl-1,3-propanediol (neopentyl glycol), 1,6-hexanediol, 2-ethyl-2-methyl-1,3-propanediol, 2,2-diethyl-1,3-propanediol, 1,8-octanediol, 2-ethyl-2-butyl-1,3-propanediol, 2-ethyl-2,4-dimethyl-1,3-hexanediol, 1,10-decanediol, polyethylene glycol, polypropylene glycol, 1,2-cyclohexanedimethanol, 1,3-cyclohexanedimethanol, 1,4-cyclohexanedimethanol, 2,2,4,4-tetramethyl-1,3-cyclobutanediol, 2,2-bis(4′β-hydroxyethoxydiphenyl)propane bis(4′-β-hydroxyethoxyphenyl)sulfone, xylylene glycol, and combinations of two or more thereof.

5. The shrink film of claim 4 , wherein the glycol modified polyester is a glycol modified polyethylene terephthalate.

6. The shrink film of claim 5 , wherein the glycol modified polyester comprises an alkylene glycol chosen from ethylene glycol, propylene glycol, butylene glycol, pentylene glycol, 1,6-hexanediol, 2,2-dimethyl-1,3-propanediol, or a combination of two or more thereof.

7. The shrink film of claim 1 , wherein the antiblocking agent is chosen from diatomaceous earth, aluminum silicates, silicon dioxide, quarts, glass, silica sand, kaolin, talc, feldspar, calcium carbonate, gel-type synthetic silica, precipitated-type synthetic silica, sodium calcium aluminosilicate, calcium silicate, metal oxides of Group 2, 3, 4, 5, 13, or 14 metals, or combinations of two or more thereof.

8. The shrink film of claim 1 , wherein the resin material of the skin layers is individually polylactic acid or a glycol modified polyethylene terephthalate material.

9. The shrink film of claim 1 , having an upper skin:core:lower skin thickness ratio of about 5:90:5.

10. The shrink film of claim 1 , wherein at least one of the upper skin layer and the lower skin layer comprises print indicia thereon.

11. The shrink film of claim 1 , wherein at least one of the upper skin layer and the lower skin layer comprises an adhesive layer thereon.

12. The shrink film of claim 1 , wherein the shrink film is oriented in the machine direction.

13. The shrink film of claim 12 , wherein the orientation ratio is from about 1.1:1 to about 4:1.

14. The shrink film of claim 12 , wherein the orientation is about 2:1 to about 3:1.

15. The shrink film of claim 1 , wherein the film has a shrink initiation temperature of about 55 to about 65° C.

16. An article encapsulated with the shrink film of claim 1 .

17. The article of claim 16 , wherein the article is a battery.

18. The shrink film of claim 1 , wherein the shrink film has a free shrink of at most about 5% 70° C. in a second different direction.

19. The shrink film of claim 1 , wherein the shrink film has a free shrink of less than 3% at about 40° C. to about 65° C. in a second different direction as measured according to ASTM D2732.

20. The shrink film of claim 1 , wherein the glass transition temperature (Tg) of the glycol modified polyester is from about 50° C. to about 100° C.

21. The shrink film of claim 1 , wherein the shrink film is clear.

22. The shrink film of claim 1 , wherein the resin material in at least one of the upper skin layer and the lower skin layer is polylactic acid.

23. The shrink film of claim 1 , wherein the skin layers each individually consist of the resin material and the antiblocking agent.

24. The shrink film of claim 1 , wherein the shrink film consists of the core layer, the upper skin layer, and the lower skin layer.