Alkaline-earth metal compound-containing zeolite catalyst, method for preparing same, method for regenerating same, and method for producing lower hydrocarbons
View Patent ↗An alkaline-earth metal compound-containing zeolite catalyst composed of a composite material comprising at least a first component, a second component, and a third component. The first component is composed of at least one of zeolites selected from a group consisting of proton-type zeolites and ammonium type zeolites. The second component is composed of at least one of alkaline-earth metal compounds. The third component is composed of at least one selected from a group consisting of aluminum oxides, aluminum hydroxides, silicon oxides, silicon hydroxides, and clay minerals. The first component has a molar ratio of Si/Al of 10 or more and 300 or less. Content of the second component relative to the first component is 0.3 mass % or more and less than 10 mass % as alkaline-earth metal. Content of the third component relative to the first component is 15 mass % or more and 200 mass % or less.
1. A method for preparing an alkaline-earth metal compound-containing zeolite catalyst, comprising:
a mixing-kneading step of adding polar solvent to a composition composed at least of a first component, a second component, and a third component, and kneading to form a mixture;
a drying-calcination step of drying and calcining the mixture to form a composite material; and
a steam treatment step of contacting the composite material obtained by the drying-calcination step with steam or a reaction atmosphere that generates steam;
wherein the first component is composed of at least one of MFI-structure zeolites selected from a group consisting of proton-type zeolites and ammonium type zeolites,
the second component is composed of calcium carbonate,
the third component is composed of at least one compound selected from a group consisting of aluminum oxides, aluminum hydroxides, silicon oxides, silicon hydroxides, and clay minerals,
the first component has a molar ratio of Si/Al of 10 or more and 300 or less,
the content of the second component relative to the first component is 0.3 mass % or more and less than 10 mass % as alkaline-earth metal,
the content of the third component relative to the first component is 15 mass % or more and 200 mass % or less, and
the extent of steam treatment in the steam treatment step is 1.92 to 16.8 in A.U., said extent of steam treatment being defined by the product of steam partial pressure in MPa and a duration of the steam treatment in hours.
2. The method for preparing an alkaline-earth metal compound-containing zeolite catalyst according to claim 1 , wherein the amount of the polar solvent relative to the amount of a composition at least containing the first component, the second component, and the third component is 10 mass % or more and 150 mass % or less.
3. The method for preparing an alkaline-earth metal compound-containing zeolite catalyst according to claim 1 , wherein drying in the drying-calcination step is performed at a temperature of 80° C. or more and 150° C. or less for a duration of 30 hours or less.
4. The method for preparing an alkaline-earth metal compound-containing zeolite catalyst according to claim 1 , wherein calcination in the drying-calcination step is performed at a temperature of 350° C. or more and 750° C. or less for a duration of not longer than 50 hours.