Vinylamine containing copolymer microparticles as additives in papermaking
View Patent ↗Surfactant mediated, free radical initiated emulsion/dispersion polymerization of n-vinylformamide with styrene or substituted styrene copolymers, and its subsequently hydrolyzed products bearing formamide, amine and styrenic functionality are disclosed. Processes for polymerization, polymer composition, and hydrolysis of such polymers are also disclosed. These polymers bearing cationic functionality can be used in papermaking applications as dry strength additives, wet strength additives, retention aids, drainage aids, sizing agent, sizing promoter and pitch and stickies control agents.
1. A process for making vinylamine-vinylformamide-styrene terpolymer additives comprising:
a) reacting vinylformamide with styrene or substituted styrene under free radical, emulsion polymerization reaction conditions;
b) producing a first polymer product which comprises randomly distributed repeating units by the formula (I) and (II):
wherein Ar is an aromatic selected from the group consisting of phenyl and phenyl substituted with alkyl, alkoxy, sulfonate, halo and pyridine or substituted pyridine; R 1 is hydrogen or alkyl; x and y are numbers greater than zero mole percent, and the sum of x and y is 100 mole percent, the ratio of x:y is in the range of from 99:1 to 50:50;
c) hydrolyzing the first polymer product with an acid or base treatment;
d) producing a second polymer product comprising randomly distributed repeating monomer units having at least two of the formula (III), (IV), (V) and (VI):
wherein,
R 2 and R 3 are H;
R 4 is H or alkyl;
m 1 and m 2 independently is a positive mole percent, and m 3 and m 4 independently is 0 to 99 mole percent, and the sum of m 1 , m 2 , m 3 and m 4 is equal to or less than the x mole percent of formula (I).
2. The process of claim 1 , wherein Ar is phenyl and R 1 is H.
3. The process of claim 1 , wherein the first polymer product is vinylformamide-styrene copolymer.
4. The process of claim 1 , wherein the emulsion polymerization reaction is carried out at temperature in the range of from about 25° C. to about 120° C.
5. The process of claim 1 , wherein the emulsion polymerization reaction is carried out at temperature in the range of from about 30° C. to about 90° C.
6. The process of claim 1 , wherein the emulsion polymerization reaction is carried out at temperature in the range of from about 60° C. to about 85° C.
7. The process of claim 1 , wherein the ratio of x:y is in the range of from 80:20 to 51:49.
8. The process of claim 1 , wherein the ratio of x:y is in the range of from 80:20 to 70:30.
9. The process of claim 1 , wherein about 10% to 99% of formamide groups of the first polymer product are subsequently hydrolyzed in step c) to introduce cationic functionality of the second polymer product of step d).
10. The process of claim 1 , wherein about 20% to 80% of formamide groups of the first polymer product are subsequently hydrolyzed in step c) to introduce cationic functionality of the second polymer product of step d).
11. The process of claim 1 , wherein about 30% to 70% of formamide groups of the first polymer product are subsequently hydrolyzed in step c) to introduce cationic functionality of the second polymer product of step d).
12. The process of claim 1 , wherein the second polymer product is a cationic, and water dispersible polymer.
13. An aqueous dispersion comprising the resulting polymer product from a process which comprises:
a) reacting vinylformamide with styrene or substituted styrene under free radical, emulsion polymerization reaction conditions
b) producing a polymer product which comprises randomly distributed repeating units by the formula (I) and (II):
wherein Ar is an aromatic selected from the group consisting of phenyl and phenyl substituted with alkyl, alkoxy, sulfonate, halo and pyridine or substituted pyridine; R 1 is hydrogen or alkyl; x and y are numbers greater than zero mole percent, and the sum of x and y is 100 mole percent, the ratio of x:y is in the range of from 99:1 to 50:50;
wherein, the polymer product in said aqueous dispersion is in a form of microparticles, and the particle size of the polymer product is in the range of from 30 nanometer to 2000 nanometer.
14. The aqueous dispersion of claim 13 , wherein the particle size of the polymer product is in the range of from 50 nm to 1000 nanometer.
15. The aqueous dispersion of claim 13 , wherein the particle size of the polymer product is in the range of from 70 nanometer to 200 nanometer.
16. A vinylamine-vinylformamide-styrene terpolymer additive comprising the resulting second polymer product from a process which comprises:
a) reacting vinylformamide with styrene or substituted styrene under free radical, emulsion polymerization reaction conditions;
b) producing a first polymer product which comprises randomly distributed repeating units by the formula (I) and (II):
wherein Ar is an aromatic selected from the group consisting of phenyl and phenyl substituted with alkyl, alkoxy, sulfonate, halo and pyridine or substituted pyridine; R 1 is hydrogen or alkyl; x and y are numbers greater than zero mole percent, and the sum of x and y is 100 mole percent, the ratio of x:y is in the range of from 99:1 to 50:50;
c) hydrolyzing the first polymer product using and acid or base treatment;
d) producing a second polymer product comprising randomly distributed repeating monomer units having at least two of the formulae (III), (IV), (V) and (VI):
wherein,
R 2 and R 3 are H
R 4 is H or alkyl;
m 1 and m 2 independently is a positive mole percent, and m 3 and m 4 independently is 0 to 99 mole percent, and the sum of m 1 , m 2 , m 3 and m 4 is equal to or less than the x mole percent of formula (I),
wherein, the first polymer product is in a form of microparticles, and the particle size of the first polymer product is in the range of from 30 nanometer to 2000 nanometer, and the second polymer product is vinylamine-vinylformamide-styrene terpolymer, and
wherein, said vinylamine-vinylformamide-styrene terpolymer additive is in a form of microparticles in aqueous dispersion, and the viscosity measured at ambient temperature (about 20° C. to about 25° C.) of active solids in the range of from 13.0% to 18.0% of vinylamine-vinylformamide-styrene terpolymer is in the range of from 100 to 500 cP.
17. The vinylamine-vinylformamide-styrene terpolymer additive of claim 16 , wherein the particle size of the first polymer product is in the range of from 50 nm to 1000 nanometer.
18. The vinylamine-vinylformamide-styrene terpolymer additive of claim 16 , wherein the particle size of the first polymer product is in the range of from 70 nanometer to 200 nanometer.
19. The vinylamine-vinylformamide-styrene terpolymer additive of claim 16 , wherein about 10% to 99% of formamide groups of the first polymer product are subsequently hydrolyzed in step c) to introduce cationic functionality of the second polymer product of step d).
20. The vinylamine-vinylformamide-styrene terpolymer additive of claim 16 , wherein about 20% to 80% of formamide groups of the first polymer product are subsequently hydrolyzed in step c) to introduce cationic functionality of the second polymer product of step d).
21. The vinylamine-vinylformamide-styrene terpolymer additive of claim 16 , wherein about 30% to 70% of formamide groups of the first polymer product are subsequently hydrolyzed in step c) to introduce cationic functionality of the second polymer product of step d).
22. The vinylamine-vinylformamide-styrene terpolymer additive of claim 16 , wherein the vinylamine-vinylformamide-styrene terpolymer additive is added to the wet end of the paper making system to improve paper making process and paper wet and dry strength.
23. The vinylamine-vinylformamide-styrene terpolymer additive of claim 16 , wherein the vinylamine-vinylformamide-styrene terpolymer additive is applied on already formed paper to improve paper finish properties.
24. A paper product comprising the second polymer product of claim 1 .
25. A paper product comprising the vinylamine-vinylformamide-styrene terpolymer additive of claim 16 .