Photochromic lens
A photochromic lens is proposed which can lose its color in a shorter period of time, and which is less likely to deteriorate when exposed to ultraviolet radiation. The photochromic lens is formed by dissolving 0.03 to 0.2 parts by mass of a spirooxazine photochromic compound in tetrahydrofuran, mixing the solution thus obtained into 100 parts by mass of a lens resin material so that the photochromic compound is uniformly dispersed in the resin material.
1. A photochromic lens for eyeglasses comprising a resin lens plastic base layer and a polarizing film integral with the resin lens plastic base layer, whereby the photochromic lens is polarized,
wherein the resin lens plastic base layer comprises 100 parts by mass of a polyurethane resin, and 0.05 to 0.12 parts by mass of a spirooxazine photochromic compound expressed by Chemical Formula 1 below
wherein the spirooxazine photochromic compound is uniformly dispersed in the resin lens plastic base layer,
wherein the polyurethane resin is obtained by adding 4,4′-methylenebis(2-chloroaniline) to a prepolymer obtained by reacting a polyisocyanate with a polyhydroxy compound to provide a mixture, and heating and curing the mixture,
wherein the resin lens plastic base layer is formed by dissolving the spirooxazine compound in tetrahydrofuran to obtain a solution, mixing the solution into the polyurethane resin to obtain a mixture, deaerating the mixture to volatilize the tetrahydrofuran to obtain a deaerated mixture, and forming the deaerated mixture into the resin lens plastic base layer by injecting the deaerated mixture into a mold, and curing the deaerated mixture,
wherein the resin lens plastic base layer has a thickness of 1 to 15 mm, and
wherein the photochromic lens is suitable as an eyeglass lens.
2. The photochromic lens of claim 1 , further comprising a protective layer formed on a surface of the resin lens plastic base layer.
3. The photochromic lens of claim 2 , wherein the protective layer contains an ultraviolet reflecting agent and an antioxidant.
4. The photochromic lens of claim 2 , wherein the protective layer comprises a first sub-layer and a second metal deposition sub-layer formed on a surface of the first sub-layer.
5. The photochromic lens of claim 3 , wherein the protective layer comprises a first sub-layer and a second metal deposition sub-layer formed on a surface of the first sub-layer.
6. The photochromic lens of claim 1 , wherein the resin lens plastic base layer is integrally laminated on the respective sides of the polarizing film layer.
7. A photochromic lens for eyeglasses consisting of a resin lens plastic base layer, a polarizing film integral with the resin lens plastic base layer, whereby the photochromic lens is polarized, and, optionally, one or more layers formed on a surface of the resin lens plastic base layer,
wherein the resin lens plastic base layer comprises 100 parts by mass of a polyurethane resin, and 0.05 to 0.12 parts by mass of an a spirooxazine photochromic compound expressed by Chemical Formula 1 below
wherein the spirooxazine photochromic compound is uniformly dispersed in the resin lens plastic base layer,
wherein the polyurethane resin is obtained by adding 4,4′-methylenebis(2-chloroaniline) to a prepolymer obtained by reacting a polyisocyanate with a polyhydroxy compound to provide a mixture, and heating and curing the mixture,
wherein the resin lens plastic base layer is formed by dissolving the spirooxazine compound in tetrahydrofuran to obtain a solution, mixing the solution into the polyurethane resin to obtain a mixture, deaerating the mixture to volatilize the tetrahydrofuran to obtain a deaerated mixture, and forming the deaerated mixture into the resin lens plastic base layer by injecting the deaerated mixture into a mold, and curing the deaerated mixture,
wherein the resin lens plastic base layer has a thickness of 1 to 15 mm, and
wherein the photochromic lens is suitable as an eyeglass lens.
8. The photochromic lens of claim 7 , consisting of a resin lens plastic base layer, a polarizing film integral with the resin lens plastic base layer, whereby the photochromic lens is polarized, and one or more layers formed on a surface of the resin lens plastic base layer, wherein the one or more layers are protective layers.
9. The photochromic lens of claim 8 , wherein the protective layers contain at least one of ultraviolet reflecting agents and antioxidants.
10. The photochromic lens of claim 8 , wherein the protective layers comprise a first sub-layer and a second metal deposition sub-layer formed on a surface of the first sub-layer.
11. The photochromic lens of claim 9 , wherein the protective layers comprise a first sub-layer and a second metal deposition sub-layer formed on a surface of the first sub-layer.
12. The photochromic lens of claim 7 , wherein the resin lens plastic base layer is integrally laminated on the respective sides of the polarizing film layer.