Vehicle-mounted heat-resistant hose
View Patent ↗A heat-resistant hose for a vehicle available at a low cost and excellent in interlayer adhesiveness includes: an inner layer; and an outer layer directly formed on an outer peripheral surface of the inner layer, in which the inner layer comprises a fluorine-based rubber composition containing the following components (a) to (e): (a) a fluorine-based rubber; (b) a polyol-based vulcanizing agent; (c) an organic onium compound; (d) magnesium oxide; and (e) calcium hydroxide, and the outer layer comprises an acrylic rubber composition containing the following components (A) to (C): (A) an acrylic rubber; (B) a benzenediol; and (C) at least one of an imidazole compound and a diamine-based vulcanizing agent.
1. A heat-resistant hose for a vehicle, comprising:
an inner layer; and
an outer layer directly formed on an outer peripheral surface of the inner layer,
wherein the inner layer comprises a fluorine-based rubber composition containing the following components (a) to (e):
(a) a fluorine-based rubber;
(b) a polyol-based vulcanizing agent;
(c) an organic onium compound;
(d) magnesium oxide; and
(e) calcium hydroxide, and
wherein the outer layer comprises an acrylic rubber composition containing the following components (A) to (C):
(A) an acrylic rubber;
(B) a benzenediol; and
(C) at least one of an imidazole compound and a diamine-based vulcanizing agent.
2. A heat-resistant hose for a vehicle according to claim 1 , wherein a content of the component (B) is 0.5 to 5 parts by weight with respect to 100 parts by weight of the component (A).
3. A heat-resistant hose for a vehicle according to claim 1 , wherein the component (c) comprises at least one of a quaternary ammonium salt and a quaternary phosphonium salt.
4. A heat-resistant hose for a vehicle according to claim 1 , wherein the component (C) comprises at least one of 1,2-dimethylimidazole and 2,2-bis[4-(4-aminophenoxy)phenyl]propane.
5. A heat-resistant hose for a vehicle according to claim 1 , wherein a content of the component (b) is 0.5 to 5 parts by weight with respect to 100 parts by weight of the component (a), a content of the component (c) is 0.2 to 4 parts by weight with respect to 100 parts by weight of the component (a), a content of the component (d) is 0.5 to 15 parts by weight with respect to 100 parts by weight of the component (a), a content of the component (e) is 1 to 15 parts by weight with respect to 100 parts by weight of the component (a), and a content of the component (C) is 0.2 to 5 parts by weight with respect to 100 parts by weight of the component (A).
6. A heat-resistant hose for a vehicle according to claim 1 , wherein the acrylic rubber composition of the outer layer further contains the following component (D) in addition to the components (A) to (C):
(D) a vulcanization accelerator,
wherein the component (D) comprises at least one of a thiourea-based vulcanization accelerator and a guanidine-based vulcanization accelerator.
7. A heat-resistant hose for a vehicle according to claim 1 , wherein the inner layer and the outer layer are subjected to direct vulcanization adhesion to each other.
8. A heat-resistant hose for a vehicle according to claim 1 , wherein the fluorine-based rubber composition is free of a benzenediol.
9. A heat-resistant hose for a vehicle according to claim 1 , wherein an outermost layer formed by using the acrylic rubber composition containing the components (A) to (C) is directly formed on an outer peripheral surface of the outer layer.
10. A heat-resistant hose for a vehicle according to claim 1 , wherein the component (B) comprises at least one selected from the group consisting of: 1,3-benzenediol (resorcinol); 1,2-benzenediol (catechol); and 1,4-benzenediol (hydroquinone).
11. A heat-resistant hose for a vehicle according to claim 10 , wherein a content of the component (B) is 0.5 to 5 parts by weight with respect to 100 parts by weight of the component (A).
12. A heat-resistant hose for a vehicle according to claim 10 , wherein the component (c) comprises at least one of a quaternary ammonium salt and a quaternary phosphonium salt.
13. A heat-resistant hose for a vehicle according to claim 10 , wherein the component (C) comprises at least one of 1,2-dimethylimidazole and 2,2-bis[4-(4-aminophenoxy)phenyl]propane.
14. A heat-resistant hose for a vehicle according to claim 10 , wherein a content of the component (b) is 0.5 to 5 parts by weight with respect to 100 parts by weight of the component (a), a content of the component (c) is 0.2 to 4 parts by weight with respect to 100 parts by weight of the component (a), a content of the component (d) is 0.5 to 15 parts by weight with respect to 100 parts by weight of the component (a), a content of the component (e) is 1 to 15 parts by weight with respect to 100 parts by weight of the component (a), and a content of the component (C) is 0.2 to 5 parts by weight with respect to 100 parts by weight of the component (A).
15. A heat-resistant hose for a vehicle according to claim 10 , wherein the acrylic rubber composition of the outer layer further contains the following component (D) in addition to the components (A) to (C):
(D) a vulcanization accelerator,
wherein the component (D) comprises at least one of a thiourea-based vulcanization accelerator and a guanidine-based vulcanization accelerator.
16. A heat-resistant hose for a vehicle according to claim 10 , wherein the inner layer and the outer layer are subjected to direct vulcanization adhesion to each other.
17. A heat-resistant hose for a vehicle according to claim 10 , wherein the fluorine-based rubber composition is free of a benzenediol.
18. A heat-resistant hose for a vehicle according to claim 10 , wherein an outermost layer formed by using the acrylic rubber composition containing the components (A) to (C) is directly formed on an outer peripheral surface of the outer layer.