Ion exchangeable glass with high crack initiation threshold
Alkali aluminosilicate glasses that are resistant to damage due to sharp impact and capable of fast ion exchange are provided. The glasses comprise at least 4 mol % P 2 O 5 and, when ion exchanged, have a Vickers indentation crack initiation load of at least about 7 kgf.
1. An alkali aluminosilicate glass comprising at least about 4% P 2 O 5 and from 0 mol % to about 4 mol % B 2 O 3 , wherein the alkali aluminosilicate glass is Li 2 O-free and wherein:
1.3<[(P 2 O 5 +R 2 O)/M 2 O 3 ]≦2.3; ii.
where M 2 O 3 =Al 2 O 3 +B 2 O 3 , and R 2 O is the sum of monovalent cation oxides present in the alkali aluminosilicate glass.
2. The alkali aluminosilicate glass of claim 1 , wherein the glass satisfies:
1.5<[(P 2 O 5 +R 2 O)/M 2 O 3 ]≦2.0.
3. The alkali aluminosilicate glass of claim 1 , wherein the glass comprises less than 1 mol % K 2 O.
4. The alkali aluminosilicate glass of claim 3 , wherein the alkali aluminosilicate glass comprises 0 mol % K 2 O.
5. The alkali aluminosilicate glass of claim 1 , wherein the glass comprises less than 1 mol % B 2 O 3 .
6. The alkali aluminosilicate glass of claim 5 , wherein the alkali aluminosilicate glass comprises 0 mol % B 2 O 3 .
7. The alkali aluminosilicate glass of claim 1 , wherein the glass is ion exchanged to a depth of layer of at least about 10 μm.
8. The alkali aluminosilicate glass of claim 7 , wherein the glass is ion exchanged to a depth of layer of at least about 30 μm.
9. The alkali aluminosilicate glass of claim 7 , wherein the alkali aluminosilicate glass has a compressive layer extending from a surface of the glass to the depth of layer, and wherein the compressive layer is under a compressive stress of at least about 300 MPa.
10. The alkali aluminosilicate glass of claim 9 , wherein the compressive stress is at least about 500 MPa.
11. The alkali aluminosilicate glass of claim 7 , wherein the ion exchanged alkali aluminosilicate glass has a Vickers indentation crack initiation load of at least about 7 kgf.
12. The alkali aluminosilicate glass of claim 11 , wherein the ion exchanged alkali aluminosilicate glass has a Vickers indentation crack initiation load of at least about 12 kgf.
13. The alkali aluminosilicate glass of claim 1 , wherein the monovalent and divalent cation oxides are selected from the group consisting of Na 2 O, K 2 O, Rb 2 O, Cs 2 O, MgO, CaO, SrO, BaO, and ZnO.
14. The alkali aluminosilicate glass of claim 1 , wherein the alkali aluminosilicate glass comprises from about 40 mol % to about 70 mol % SiO 2 ; from about 11 mol % to about 25 mol % Al 2 O 3 ; from about 4 mol % to about 15 mol % P 2 O 5 ; and from about 13 mol % to about 25 mol % Na 2 O.
15. The alkali aluminosilicate glass of claim 14 , wherein the alkali aluminosilicate glass comprises from about 50 mol % to about 65 mol % SiO 2 ; from about 14 mol % to about 20 mol % Al 2 O 3 ; from about 4 mol % to about 10 mol % P 2 O 5 ; and from about 14 mol % to about 20 mol % Na 2 O.
16. The alkali aluminosilicate glass of claim 14 , wherein the alkali aluminosilicate glass comprises less than 1 mol % K 2 O.
17. The alkali aluminosilicate glass of claim 16 , wherein the alkali aluminosilicate glass comprises 0 mol % K 2 O.
18. The alkali aluminosilicate glass of claim 14 , wherein the alkali aluminosilicate glass comprises less than 1 mol % B 2 O 3 .
19. The alkali aluminosilicate glass of claim 16 , wherein the alkali aluminosilicate glass comprises 0 mol % B 2 O 3 .
20. The alkali aluminosilicate glass of claim 1 , wherein the alkali aluminosilicate glass has a potassium/sodium interdiffusion coefficient of at least about 2.4×10 −10 cm 2 /s at 410° C.
21. The alkali aluminosilicate glass of claim 20 , wherein the potassium/sodium interdiffusion coefficient is in a range from about 2.4×10 −10 cm 2 /s up to about 1.5×10 −9 cm 2 /s at 410° C.