Film structure with high oxygen barrier properties and method of manufacturing such a film structure
View Patent ↗Film structure of at least five layers, two outer layers ( 2 ) made of a polyolefin on which is each time provided, on the opposite sides, a layer ( 4 ) forming a gas barrier and whereby, between both above-mentioned gas barriers ( 4 ), is provided a layer ( 3 ) made of a foamed synthetic material, whereby the outer layers ( 2 ) consist of a mixture of a polyolefin and a binder, which makes it possible to bond this polyolefin with the layer ( 4 ) forming the gas barrier.
1. A method for manufacturing a film structure, which method comprises co-extruding a multi-layered film structure comprising at least five layers, including two outer layers ( 2 ) made of a polyolefin, on each of which is provided, on opposite sides a layer ( 4 ) forming a gas barrier, and wherein, between both gas barriers is provided a layer ( 3 ) made of a foamed synthetic material, the method including mixing base material for the two outer layers ( 2 ) of polyolefin with binder which makes it possible to bond the polyolefin layers ( 2 ) with the above-mentioned barrier layers ( 4 ).
2. The method according to claim 1 , wherein the layer ( 3 ) is a polyolefin foam layer.
3. The method according to claim 2 , including mixing binder with the foamed synthetic material to bond the layer ( 3 ) to the gas barrier layers ( 4 ).
4. The method according to claim 3 , wherein the gas barrier ( 4 ) is made of at least an ethyl vinyl alcohol co-polymer (EVOH) or of a mixture of several EVOH co-polymers.
5. The method according to claim 2 , wherein the layers ( 2 , 3 ) and the layers ( 4 ) are extruded together by means of co-extrusion.
6. The method according to claim 2 , wherein the polyolefin is a polyethylene.
7. The method according to claim 2 , wherein the binder is a modified polyolefin.
8. The method according to claim 4 , wherein between the outer layers ( 2 ) and the gas barriers ( 4 ) is an oxygen-binding layer ( 11 ).
9. A method of manufacturing a co-extruded multi-layer film structure comprising:
coextruding a multi-layer film structure of at least five layers, wherein the layers comprise in relative order:
a) a first outer layer made from a mixture of polyolefin and a binder for binding the outer layer to an adjacent first gas barrier layer;
b) a first gas barrier layer made of an ethylene vinyl alcohol (EVOH) copolymer;
c) a polyolefin foam layer made from a mixture of a polyolefin and a binder to enhance bonding of the foam layer with adjacent first and second gas barrier layers;
d) a second gas barrier layer made of an ethylene vinyl alcohol (EVOH) co-polymer;
e) a second outer layer made of a mixture of a polyolefin and a binder for bonding the outer layer to the adjacent second gas barrier layer.
10. The method of claim 9 , wherein each outer layer has a thickness of between 25 and 300 μm.
11. The method of claim 10 , wherein each outer layer has a thickness of between 150 and 200 μm.
12. The method of claim 9 , wherein the EVOH co-polymer comprises 48 mole percent polyethylene, or a mixture of two EVOH co-polymers where the mole percentage of each EVOH co-polymer is between 32-48 mole percent polyethylene.
13. The method of claim 9 , wherein the EVOH gas barrier layers each have a thickness between 5 and 100 μm.
14. The method of claim 9 , wherein the binder is a modified polyolefin.
15. The method of claim 9 , wherein the binder includes between 5 and 20 mass percent of functional groups.
16. The method of claim 9 , wherein the foam layer is made of a polyethylene.
17. The method of claim 16 , wherein the polyethylene is low density polyethylene.
18. The method of claim 9 , wherein the co-extruded multilayer film structure comprises a supple, elastic thick film structure in the form of a slice suitable for fixing by mechanical clamping or adhesive to a cap for sealing the cap to the neck of a bottle in a leak-tight manner.