Resin composition for high barrier paper-coating
View Patent ↗Provided is a resin composition for paper-coating comprising aliphatic polycarbonate having an average molecular weight of 30,000 to 300,000 obtained by reaction of one or at least two different kinds of epoxide compounds selected from a group consisting of (C2-C10)alkylene oxide substituted or unsubstituted with carbon dioxide, halogen, or alkoxy; (C4-C20)cycloalkylene oxide substituted or unsubstituted with halogen or alkoxy; and (C8-C20)styrene oxide substituted or unsubstituted with halogen, alkoxy, alkyl or aryl, wherein it contains 0 to 40 weight % of polyolefin-based resin such as polyethylene or polypropylene, based on the total amount of the composition. In addition, the present invention relates to a paper coating method of extrusion-coating the resin composition for paper-coating on paper at 130 to 250° C. to manufacture a coated paper.
1. A resin composition for paper-coating comprising:
30 to 40 weight %, based on the total amount of the composition, of a polyolefin-based resin including a mixture of homo polypropylene and low-density polyethylene and 60 to 70 weight %, based on the total amount of the composition, of an aliphatic polycarbonate resin having an average molecular weight of 30,000 to 300,000 obtained by reacting carbon dioxide with at least one epoxide compound selected from a group consisting of (C2-C10)alkylene oxide substituted or unsubstituted with halogen or alkoxy; (C4-C20)cycloalkylene oxide substituted or unsubstituted with halogen or alkoxy; and (C8-C20)styrene oxide substituted or unsubstituted with halogen, alkoxy, alkyl or aryl.
2. The resin composition for paper-coating of claim 1 , wherein the polyolefin-based resin has a melt index (MI) of 0.5 to 100.
3. The resin composition for paper-coating of claim 1 , wherein the aliphatic polycarbonate is represented by the following Chemical Formula 1.
4. The resin composition for paper-coating of claim 1 , wherein the aliphatic polycarbonate has a melt index (MI, 150° C./5 kg) of 0.1 to 20.
5. The resin composition for paper-coating of claim 1 , further comprising:
one additive selected from a pigment, a dye, a filler, an antioxidant, a sunscreen agent, an antistatic agent, an anti-blocking agent, a slip agent, an inorganic filler, a compatibilizer, a stabilizer, a tackifier resin, a modified resin, a leveling agent, a fluorescent whitening agent, a dispersant, a heat stabilizer, a photo-stabilizer, an ultraviolet absorber, and a lubricant.
6. A paper coating method of extrusion-coating the resin composition for paper-coating of claim 1 on paper at 130 to 250° C. to manufacture a coated paper.
7. A paper coating method of extrusion-coating the resin composition for paper-coating of claim 2 on paper at 130 to 250° C. to manufacture a coated paper.
8. A paper coating method of extrusion-coating the resin composition for paper-coating of claim 3 on paper at 130 to 250° C. to manufacture a coated paper.
9. A paper coating method of extrusion-coating the resin composition for paper-coating of claim 4 on paper at 130 to 250° C. to manufacture a coated paper.
10. A paper coating method of extrusion-coating the resin composition for paper-coating of claims 5 on paper at 130 to 250° C. to manufacture a coated paper.
11. The paper coating method of claim 6 , wherein at the time of coating, a coating thickness is 1 to 50 μm.
12. The paper coating method of claim 7 , wherein at the time of coating, a coating thickness is 1 to 50 μm.
13. The paper coating method of claim 8 , wherein at the time of coating, a coating thickness is 1 to 50 μm.
14. The paper coating method of claim 9 , wherein at the time of coating, a coating thickness is 1 to 50 μm.
15. The paper coating method of claim 10 , wherein at the time of coating, a coating thickness is 1 to 50 μm.