Temperature-stable liquid aqueous polysaccharide suspensions and use thereof as thickening agents in cementitious compositions
A liquid aqueous suspension of polysaccharide, contains a mass concentration of at least one polysaccharide of between 15 and 35% in the form of partially hydrated particles dispersed in an aqueous solution of a strong base salt, excluding ammonium salts, with an ionic strength of between 1.25 mol/L and 15 mol/L, has a pH greater than 9 and contains at least one non-phyllitic crystalline mineral powder, referred to hereafter as filler, which is chemically inert in the aqueous suspension and which has a grain size of between 0.1 and 100 micrometers and an attapulgite in micronized form, the aqueous suspension being stable at least in a temperature range from 5 to 30° C. The suspension is suitable for use as an agent for thickening cementitious compositions.
1. A cementitious composition based on cement and water, comprising, as viscosifying agent, a liquid aqueous polysaccharide suspension in a content of between 0.1 and 5% by weight of cement,
wherein said liquid aqueous polysaccharide suspension comprises:
a concentration by weight of at least one polysaccharide of between 15 and 35% in the form of partially hydrated particles dispersed in an aqueous solution of a strong base salt, with the exception of ammonium salts, having an ionic strength of between 1.25 mol/l and 15 mol/l, exhibiting a pH of greater than 9, and
an attapulgite in the micronized form and at least one nonphyllitic mineral powder as a filler, chemically inert in said liquid aqueous polysaccharide suspension, with a particle size of between 0.1 and 100 micrometers, conferring on said liquid aqueous polysaccharide suspension a stability at least in a temperature range extending from 5 to 30° C.
2. The cementitious composition as claimed in claim 1 , wherein the content by weight of attapulgite is between 0.1% and 5% in said liquid aqueous polysaccharide suspension.
3. The cementitious composition as claimed in claim 1 , wherein the aqueous solution exhibits an ionic strength of between 2.5 mol/l and 12.5 mol/l.
4. The cementitious composition as claimed in claim 1 , wherein the filler is a siliceous filler with a density of between 2.60 and 2.80 g/ml.
5. The cementitious composition as claimed in claim 1 , wherein the filler exhibits a particle size curve for which the D50 value is between 1 and 12 micrometers.
6. The cementitious composition as claimed in claim 1 , wherein the content by weight of filler is between 0.1 and 5% of said liquid aqueous polysaccharide suspension.
7. The cementitious composition as claimed in claim 1 , wherein the concentration by weight of polysaccharide(s) is between 18 and 25% of said liquid aqueous polysaccharide suspension.
8. The cementitious composition as claimed in claim 1 , wherein the polysaccharide exhibits, dry, a particle size curve for which the D50 value is between 10 and 200 μm.
9. The cementitious composition as claimed in claim 1 , wherein the polysaccharide is selected from the group consisting of a hydroxyalkylcellulose or a hydroxyalkyl guar comprising a C 2 to C 8 alkyl group, a diutan gum and mixtures thereof.
10. The cementitious composition as claimed in claim 9 , wherein the hydroxyalkylcellulose is selected from the group consisting of a hydroxyethylcellulose (HEC), a methylhydroxypropyl cellulose (MHPC), a hydrophobic modified hydroxyethylcellulose (HMHEC) and mixtures thereof.