Black particles and a manufacturing method of the same, a black toner using the same, and a particle container and a toner container
View Patent ↗Black particles include a black pigment; and a cyan pigment, wherein when the reflectance to light of wavelength of 420 nm and the reflectance to light of wavelength of 770 nm of plural samples are measured, the standard deviations (1σ) of the measured values are about 1 or less with respect to both wavelengths.
1. Black particles comprising:
a black pigment; and
a cyan pigment,
wherein
the black pigment and the cyan pigment are unified in the form of agglomerate.
2. The black particles as claimed in claim 1 , wherein
when the reflectance to light of wavelength of 420 nm and the reflectance to light of wavelength of 770 nm of a plurality of samples are measured, the difference between the average of the reflectance to light of wavelength of 420 nm and the average of the reflectance to light of wavelength of 770 nm is within about 5%.
3. The black particles as claimed in claim 1 , wherein
the blending proportion of the black pigment and the cyan pigment is in the range of about 10/1 to about 2/1 by mass ratio.
4. The black particles as claimed in claim 1 , which have a number average particle size of about 1 μm or less.
5. The black particles as claimed in claim 1 , wherein
the cyan pigment is C.I. Pigment Blue 15:3.
6. A method for manufacturing the black particles as claimed in claim 1 , the method comprising:
mixing the black pigment and the cyan pigment; and
performing a compaction molding while applying load to the mixture of the black pigment and the cyan pigment.
7. The manufacturing method of the black particles as claimed in claim 6 , wherein
an apparatus selected from the group consisting of a ball mill, a turbo crusher, a screen mill and a jet crusher is used for the compaction molding while applying load to the mixture of the black pigment and the cyan pigment.
8. A black toner comprising:
the black particles as claimed in claim 1 ; and
a binder resin.
9. The black toner as claimed in claim 8 , wherein
the binder resin is a polyester resin.
10. The black toner as claimed in claim 8 , wherein
the binder resin has a glass transition temperature (Tg) of about 50° C. to about 80° C.
11. The black toner as claimed in claim 8 , wherein
the binder resin has a softening temperature of about 90° C. to about 150° C.
12. The black toner as claimed in claim 8 , wherein
the binder resin has a mass average molecular weight of about 8,000 to about 15,000.
13. The black toner as claimed in claim 8 , wherein
the blending proportion of the black particles to the total mass of the solid contents constituting the toner is from about 1 mass % to about 15 mass %.
14. A toner container for storing the black toner as claimed in claim 8 .