High-strength and high-toughness ultrafine wire rod
Provided is an ultra-fine grained, high-strength, high-toughness carbon steel wire rod manufactured through control of a microstructure by process control without addition of relatively expensive alloying elements. More particularly, the material provided is an ultra-fine grained, high-strength, high-toughness carbon steel wire rod having a microstructure including a ferrite structure having an area fraction of 60% or more and a cementite structure as a remainder, wherein an average grain diameter of ferrite grains is 15 μm or less. Also provided is a method of manufacturing the wire rod.
1. An ultra-fine grained, high-strength, high-toughness wire rod having a microstructure comprising:
a ferrite structure having an area fraction of 60% or more; and
a cementite structure as a remainder,
wherein an average grain diameter of ferrite grains is 15 μm or less and the ferrite grains have a shape of bainitic ferrite,
wherein the wire rod comprises 0.15 wt % to 0.5 wt % of carbon (C), 0.1 wt % to 0.2 wt % of silicon (Si), 0.1 wt % to 0.7 wt % of manganese (Mn), and iron (Fe) as well as other unavoidable impurities as a remainder.
2. The ultra-fine grained, high-strength, high-toughness wire rod of claim 1 , wherein the ferrite has a crystal orientation measured by electron backscattered diffraction (EBSD) of 30 degrees or less.
3. The ultra-fine grained, high-strength, high-toughness wire rod of claim 1 , wherein the wire rod has a tensile strength of 1100 MPa or more and an elongation of 20% or more.
4. The ultra-fine grained, high-strength, high-toughness wire rod of claim 1 , wherein the wire rod has an ECO-index (tensile strength×ductility) of 2000 or more.