Dental molded product for milling and manufactual method thereof
View Patent ↗Dental molded product for milling having excellent aesthetic quality, compatibility for machine and moldability from the moldable composition is provided. The dental molded product for milling is obtained by curing the moldable composition which includes a polymerizable monomer, a polymerization initiator, a first spherical inorganic filler and a second spherical inorganic filler. An average particle size of the first spherical inorganic filler is in the range of 0.2 to 10 μm. A content of the first spherical inorganic filler is in the range of 50 to 85 mass %. An average particle size of the second spherical inorganic filler is in the range of 0.005 to 0.1 μm. A content of the second spherical inorganic filler is in the range of 1 to 18 mass %.
1. A dental molded product for milling,
wherein said dental molded product for milling is obtained by curing a moldable composition,
wherein said moldable composition comprises;
a polymerizable monomer,
a polymerization initiator,
a first spherical inorganic filler, and
a second spherical inorganic filler,
wherein said first spherical inorganic filler has an average particle size in the range of 0.2 to 10 μm and is included in a content of 60 to 85 mass %,
wherein said second spherical inorganic filler has an average particle size in the range of 0.005 to 0.1 μm and is included in a content of 1 to 18 mass %, and
wherein said polymerizable monomer comprises a polyethylene glycol dimethacrylate in the range of 6 to 30 mass %, said polyethylene glycol dimethacrylate having a molecular weight in the range of 300 to 780.
2. The dental molded product for milling according to claim 1 , wherein said polymerizable monomer further comprises a triethylene glycol dimethacrylate in a content of 1 to 60 mass %.
3. A manufactural method of the dental molded product for milling according to claim 1 , wherein said manufactural method comprises;
a preparation process of preparing the moldable composition,
a filling process of filling the moldable composition in a molding die,
a degassing process of degassing the moldable composition with a decompression in the molding die, and
a curing process of curing the moldable composition in the molding die under a pressure of a normal pressure to 40 MPa.
4. A manufactural method of the dental molded product for milling according to claim 2 , wherein said manufactural method comprises;
a preparation process of preparing the moldable composition,
a filling process of filling the moldable composition in a molding die,
a degassing process of degassing the moldable composition with a decompression in the molding die, and
a curing process of curing the moldable composition in the molding die under a pressure of a normal pressure to 40 MPa.
5. A manufactural method of the dental molded product for milling according to claim 3 , wherein said manufactural method comprises;
a preparation process of preparing the moldable composition,
a filling process of filling the moldable composition in a molding die,
a degassing process of degassing the moldable composition with a decompression in the molding die, and
a curing process of curing the moldable composition in the molding die under a pressure of a normal pressure to 40 MPa.