Process for the production of PA-410 and PA-410 obtainable by that process
A process for the production of a polymer containing monomer units of butane-1,4-diamine and 1,10-decanedioic acid (PA-410) having a viscosity number (VN) of at least 105 ml/gram includes making a solution of a salt of butane-1,4-diamine and 1,10-decanedioic acid in water, concentrating the solution of the salt at a temperature of between 100 and 180° C. and a pressure of between 1.0 and 3.0 bar to a water content of between 4 and 8 wt %, producing a prepolymer from the salt containing monomer units of butane-1,4-diamine and 1,10-decanedioic acid at a temperature of between 185 and 205° C., and thereafter subjecting the prepolymer to post condensation.
1. A process for the production of a polymer containing monomer units of butane-1,4-diamine and 1,10-decanedioic acid (PA-410) comprising the steps of:
1) making an aqueous salt solution comprising a salt of butane-1,4-diamine and 1,10-decanedioic acid in water,
2) concentrating the aqueous salt solution at a temperature of between 100 and 180° C. and at a pressure of between 0.8 and 6.0 bar to achieve a water content of the aqueous salt solution of between 2 and 8 wt %,
3) producing from the salt a prepolymer containing monomer units of butane-1,4-diamine and 1,10-decanedioic acid at a temperature of between 185 and 205° C., and thereafter
4) subjecting the prepolymer to post-condensation to obtain a PA410 polymer having a viscosity number (VN) of at least 100 ml/gram as measured according to ISO 307, version 2007, in 90 wt. % formic acid at 25° C.
2. The process according to claim 1 , wherein the temperature employed in step 2) to concentrate the aqueous salt solution is between 120 and 160° C.
3. The process according to claim 1 , wherein step 2) is practiced by concentrating the aqueous salt solution to a water content of between 5 and 7 wt. %.
4. The process according to claim 1 , wherein the temperature employed in step 3) to produce the prepolymer is between 190 and 200° C.
5. A polymer comprising monomer units of butane-1,4-diamine and 1,10-decanedioic acid (PA-410) having a viscosity number (VN) of at least 105 ml/gram as measured according to ISO 307, version 2007, in 90 wt. % formic acid at 25° C.
6. The PA-410 according to claim 5 , wherein VN is at least 110 ml/gram.
7. The PA-410 according to claim 5 , wherein
([acid end groups]+[amine end groups])> b−a· VN (formulae I),
whereby [acid end groups] is the concentration of acid end groups in the polymer in meq/kg, and [amine end groups] is the concentration of amine end groups in the polymer in meq/kg, a is equal to 0.77 and b is equal to 160 and VN is the viscosity number in ml/gram.
8. The PA-410 according to claim 7 , wherein b is equal to 165.
9. The PA-410 according to claim 7 , wherein [acid end groups] and [amine end groups] are present according to formulae I such that [acid end groups]+[amine end groups]>20 meq/kg.
10. A shaped article comprising the PA-410 according to claim 5 .
11. The shaped article according to claim 10 , which is produced by an extrusion process.
12. A polymer comprising monomer units of butane-1,4-diamine and 1,10-decanedioic acid (PA-410) which is produced by the process according to claim 1 .