Low-alloy steel having a high yield strength and a high sulphide-induced stress cracking resistance
View Patent ↗A steel contains, by weight: C: 0.3% to 0.5%, Si: 0.1% to 0.5%, Mn: 1% or less, P: 0.03% or less, S: 0.005% or less, Cr: 0.3% to 1%, Mo: 1% to 2%, W: 0.3% to 1%, V: 0.03% to 0.25%, Nb: 0.01% to 0.15%, Al: 0.01% to 0.1%, the remainder of the chemical composition of the steel being constituted by Fe and impurities or residuals resulting from or necessary to steel production and casting processes. The steel can be used to produce seamless tubes for hydrocarbon wells with a yield strength after heat treatment of 862 MPa or more or even 965 MPa or more.
1. A light alloy steel, comprising, by weight:
C: 0.3% to 0.5%;
Si: 0.1% to 1%;
Mn: 1% or less;
P: 0.03% or less;
S: 0.005% or less;
Cr: 0.3% to 1%;
Mo: 1.29% to 2%;
W: 0.52% to 1%;
V: 0.03% to 0.25%;
Nb: 0.01% to 0.15%;
Al: 0.01% to 0.1%; and
Fe;
wherein
a microstructure of the light alloy steel consists of a martensitic structure, and
Ti is not deliberately added and is an impurity obtained from the steel production such that the content of Ti is less than 0.005%.
2. The steel according to claim 1 , wherein the C content is from 0.32% to 0.38%.
3. The steel according to claim 1 , wherein the C content is from 0.40% to 0.45%.
4. The steel according to claim 1 , wherein the Mn content is from 0.2% to 0.5%.
5. The steel according to claim 1 , wherein the Cr content is from 0.3% to 0.8%.
6. The steel according to claim 1 , wherein the V content is from 0.1% to 0.25%; and the Nb content is from 0.01% to 0.03%.
7. The steel according to claim 1 , wherein a V+2×Nb content is in the range 0.10% to 0.35%.
8. The steel according to claim 1 , wherein N is not deliberately added and is an impurity obtained from the steel production such that the content of N is 0.01% or less.
9. The steel according to claim 1 , wherein the steel is quench and temper heat treated so that its yield strength is 862 MPa (125 ksi) or more.
10. The steel according to claim 1 , wherein the steel is quench and temper heat treated so that its yield strength is 965 MPa (140 ksi) or more.
11. The steel according to claim 9 , wherein the temper heat treatment comprises two quench operations.
12. The steel according to claim 1 , wherein a yield strength is 862 MPa or higher and when tested in an European Federation of Corrosion (EFC) type 16 bath for sulfide stress cracking characteristics, specimens not breaking after 720 hours are obtained.
13. The steel according to claim 10 , wherein the temper heat treatment comprises two quench operations.