Production method of acrylic polymer, acrylic polymer obtained by this production method and plastisol composition using the same
View Patent ↗A method of producing an acrylic polymer comprising a step of emulsion-polymerizing an acrylic monomer mixture (A) and a step of emulsion-polymerizing an acrylic monomer mixture (B) in the presence of a polymerization initiator and a polymerization inhibitor in amounts satisfying the following formula (1) in the polymer dispersion (D) obtained by the emulsion polymerization thereof, wherein the mass ratio (A)/(B) of the acrylic monomer mixture (A) to the acrylic monomer mixture (B) is 70/30 to 95/5; an acrylic polymer obtained by this production method; and a plastisol composition using the same. 0.1≦ Q/I ≦30 (1) in the formula (1), Q represents the molar amount of the polymerization inhibitor and I represents the molar amount of the polymerization initiator present in the polymer dispersion (D) before the introduction of the polymerization inhibitor.
1. A method of producing an acrylic polymer comprising
emulsion-polymerizing an acrylic monomer mixture (A) comprising methyl methacrylate and butyl methacrylate, wherein the total mass of the methyl methacrylate and the butyl methacrylate is 50% or more; and
emulsion-polymerizing an acrylic monomer mixture (B) in the presence of a polymerization initiator and a polymerization inhibitor in amounts satisfying the following formula (1) in a polymer dispersion (D) obtained by the emulsion polymerization of the acrylic monomer mixture (A),
0.1 ≦Q/I≦ 30 (1)
wherein the mass ratio (A)/(B) of the acrylic monomer mixture (A) to the acrylic monomer mixture (B) is 70/30 to 95/5, and
wherein Q in the formula (1) represents the molar amount of the polymerization inhibitor and I represents the molar amount of the polymerization initiator present in the polymer dispersion (D) at the time the polymerization inhibitor is introduced.
2. The method according to claim 1 , wherein the solubility parameter (SA) of the polymer (A) obtained by polymerizing the acrylic monomer mixture (A) is smaller than the solubility parameter (SB) of the polymer (B) obtained by polymerizing the acrylic monomer mixture (B).
3. The method according to claim 1 , wherein the mass ratio of the methyl methacrylate to the butyl methacrylate is in a range of 20/80 to 75/25.
4. An acrylic polymer obtained by the method according to claim 3 .
5. A plastisol composition comprising the acrylic polymer according to claim 4 and a plasticizer.