Process for preparing a thixotroping agent and use thereof

1. A process for preparing a thixotropic agent based on a urea derivative, wherein the components

α) comprising at least one amine and

β) comprising at least one isocyanate,

are supplied separately to a mixer and are mixed with one another, wherein components α) and β) are introduced with a pressure of at least 40 to 200 bar into the mixer, the reaction mixture being discharged by spraying or squirting from the mixer.

2. The process according to claim 1 , wherein this mixer is a spray head.

3. The process according to claim 1 , wherein the molar ratio of the amine groups of the amine-comprising component to the isocyanate groups of the isocyanate-comprising component is 5:1 to 1:5.

4. The process according to claim 1 , wherein the amine of component α) comprises N-n-alkylamine and/or N-n-alkenylamine and/or secondary N-alkylamine having 1 to 22 carbon atoms and/or polyetheramines.

5. The process according to claim 1 , wherein the isocyanate of component β) comprises: hexamethylene 1,6-diisocyanate (HDI); 1-isocyanato-3,3,5-trimethyl-5-isocyanatomethylcyclohexane (IPDI); 2,4- and/or 2,6-tolylene diisocyanate (TDI) and/or 4,4′-, 2,4′- and/or 2,2′-diphenylmethane diisocyanate (MDI); m-xylene diisocyanate (MXDI); m- or p-tetramethylxylene diisocyanate (m-TMXDI, p-TMXDI); polyisocyanate comprising isocyanurates of HDI, NCO content: 23.4% by weight, viscosity 1200 mPa/s at 23° C.; 4,4′-dicyclohexylmethane diisocyanate (H12MDI); naphthalene 1,5-diisocyanate; cyclohexane 1,4-diisocyanate; hydrogenated xylylene diisocyanate (H6XDI); 1-methyl-2,4-diisocyanatocyclohexane; tetramethoxybutane 1,4-diisocyanate; butane 1,4-diisocyanate; 1,6-diisocyanato-2,2,4-trimethylhexane; 1,6-diisocyanato-2,4,4-trimethylhexane; 1-isocyanato-1-methyl-4(3)-isocyanatomethylcyclohexane (IMCI); 1,12-dodecane diisocyanate (C12DI) or mixtures thereof.

6. A process for preparing a thixotropic agent based on a urea derivative, wherein the components

α) comprising at least one amine and

β) comprising at least one isocyanate, are supplied separately to a mixer and are mixed with one another, wherein the mixture of

α) comprising at least one amine and β) comprising at least one isocyanate, after leaving the mixer, is spray-applied, squirt-applied, squirt-introduced or spray-introduced (in)to a composition;

wherein the process is carried out continuously or discontinuously; and wherein the thixotropic agent is introduced into the composition in an amount of 0.05 to 40% by weight, based on the total mass of the composition.

7. The process according to claim 6 , wherein the degree of conversion of α) amine with β) isocyanate on spray application or squirt application prior to contact with the composition is at least 75%, with respect, where appropriate, to the component used in deficit proportion.

8. A composition produced according to a process for preparing a thixotropic agent based on a urea derivative, wherein the components

α) comprising at least one amine and

β)comprising at least one isocyanate,

are supplied separately to a mixer and are mixed with one another,

wherein the mixture of α) comprising at least one amine and β) comprising at least one isocyanate, being discharged by spraying or squirting from the mixer, is spray-applied, squirt-applied, squirt-introduced or spray-introduced (in)to the composition.

9. A process for preparing a thixotropic agent based on a urea derivative, wherein the components

α) comprising at least one amine and

β) comprising at least one isocyanate,

are supplied separately to a mixer and are mixed with one another, the reaction mixture being discharged by spraying or squirting from the mixer, wherein the mixture of α) comprising at least one amine and β) comprising at least one isocyanate, after leaving the mixer, is comminuted in an apparatus.

10. The process according to claim 9 , wherein the comminuted product is introduced into a composition.

11. The process comprising using a composition according to claim 10 as an adhesive or sealant, coating material or coating.

12. The composition of claim 8 , wherein said composition comprises an adhesive or sealant, comprising said thixotropic agent and at least one curable binder.

13. The composition of claim 12 , wherein said at least one curable binder comprises epoxides, polyurethanes, acrylates, silylated polyurethanes, silylated acrylates, silylated polyureas, silyl-terminated polyethers, and silylated polysulfides.

14. The composition of claim 12 , wherein said at least one curable binder comprises polyurethane.

15. The process of claim 11 , wherein said composition comprises an adhesive or sealant, comprising said thixotropic agent and at least one curable binder.

16. The process of claim 15 , wherein said at least one curable binder comprises epoxides, polyurethanes, acrylates, silylated polyurethanes, silylated acrylates, silylated polyureas, silyl-terminated polyethers, and silylated polysulfides.

17. The process of claim 15 , wherein said at least one curable binder comprises polyurethane.

18. The process of claim 9 , wherein the amine of component α) comprises N-n-alkylamine and/or N-n-alkenylamine and/or secondary N-alkylamine having 1 to 22 carbon atoms and/or polyetheramines; and/or,

wherein the isocyanate of component β) comprises: hexamethylene 1,6-diisocyanate (HDI); 1-isocyanato-3,3,5-trimethyl-5-isocyanatomethylcyclohexane (IPDI); 2,4- and/or 2,6-tolylene diisocyanate (TDI) and/or 4,4′-, 2,4′- and/or 2,2′-diphenylmethane diisocyanate (MDI); m-xylene diisocyanate (MXDI); m- or p-tetramethylxylene diisocyanate (m-TMXDI, p-TMXDI); polyisocyanate comprising isocyanurates of HDI, NCO content: 23.4% by weight, viscosity 1200 mPa/s at 23° C.; 4,4′-dicyclohexylmethane diisocyanate (H12MDI); naphthalene 1,5-diisocyanate; cyclohexane 1,4-diisocyanate; hydrogenated xylylene diisocyanate (H6XDI); 1-methyl-2,4-diisocyanatocyclohexane; tetramethoxybutane 1,4-diisocyanate; butane 1,4-diisocyanate; 1,6-diisocyanato-2,2,4-trimethylhexane; 1,6-diisocyanato-2,4,4-trimethylhexane; 1-isocyanato-1-methyl-4(3) -isocyanatomethylcyclohexane (IMCI); 1,12-dodecane diisocyanate (C12DI) or mixtures thereof.

19. The composition of claim 8 , wherein the amine of component α) comprises N-n-alkylamine and/or N-n-alkenylamine and/or secondary N-alkylamine having 1 to 22 carbon atoms and/or polyetheramines; and/or,

wherein the isocyanate of component β) comprises: hexamethylene 1,6-diisocyanate (HDI); 1-isocyanato-3,3,5-trimethyl-5-isocyanatomethylcyclohexane (IPDI); 2,4- and/or 2,6-tolylene diisocyanate (TDI) and/or 4,4′-, 2,4′- and/or 2,2′-diphenylmethane diisocyanate (MDI); m-xylene diisocyanate (MXDI); m- or p-tetramethylxylene diisocyanate (m-TMXDI, p-TMXDI); polyisocyanate comprising isocyanurates of HDI, NCO content: 23.4% by weight, viscosity 1200 mPa/s at 23° C.; 4,4′-dicyclohexylmethane diisocyanate (H12MDI); naphthalene 1,5-diisocyanate; cyclohexane 1,4-diisocyanate; hydrogenated xylylene diisocyanate (H6XDI); 1-methyl-2,4-diisocyanatocyclohexane; tetramethoxybutane 1,4-diisocyanate; butane 1,4-diisocyanate; 1,6-diisocyanato-2,2,4-trimethylhexane; 1,6-diisocyanato-2,4,4-trimethylhexane; 1-isocyanato-1-methyl-4(3) -isocyanatomethylcyclohexane (IMCI); 1,12-dodecane diisocyanate (C12DI) or mixtures thereof.

20. The process of claim 6 , wherein the amine of component α) comprises N-n-alkylamine and/or N-n-alkenylamine and/or secondary N-alkylamine having 1 to 22 carbon atoms and/or polyetheramines; and/or,

wherein the isocyanate of component β) comprises: hexamethylene 1,6-diisocyanate (HDI); 1-isocyanato-3,3,5-trimethyl-5-isocyanatomethylcyclohexane (IPDI); 2,4- and/or 2,6-tolylene diisocyanate (TDI) and/or 4,4′-, 2,4′- and/or 2,2′-diphenylmethane diisocyanate (MDI); m-xylene diisocyanate (MXDI); m- or p-tetramethylxylene diisocyanate (m-TMXDI, p-TMXDI); polyisocyanate comprising isocyanurates of HDI, NCO content: 23.4% by weight, viscosity 1200 mPa/s at 23° C.; 4,4′-dicyclohexylmethane diisocyanate (H12MDI); naphthalene 1,5-diisocyanate; cyclohexane 1,4-diisocyanate; hydrogenated xylylene diisocyanate (H6XDI); 1-methyl-2,4-diisocyanatocyclohexane; tetramethoxybutane 1,4-diisocyanate; butane 1,4-diisocyanate; 1,6-diisocyanato-2,2,4-trimethylhexane; 1,6-diisocyanato-2,4,4-trimethylhexane; 1-isocyanato-l-methyl-4(3) -isocyanatomethylcyclohexane (IMCI); 1,12-dodecane diisocyanate (C12DI) or mixtures thereof.