Method of fabricating a patterned solid polymeric electrolyte

1. A method of fabricating a solid polymeric electrolyte having a pattern, comprising the steps of, in the order recited:

mixing constituents including a liquid electrolyte, a photo-crosslinking agent, and inorganic particles to form an electrolyte paste;

dispersing together the constituents of the electrolyte paste;

coating the electrolyte paste on a substrate;

pressing the electrolyte paste with a patterned mold having a shape to copy the shape of the patterned mold onto the electrolyte paste and provide said pattern; and

illuminating an ultraviolet light onto the electrolyte paste to induce a photo-crosslinking reaction and cure the photo-crosslinking agent of the electrolyte paste,

wherein said solid polymeric electrolyte, comprises:

a polymer matrix having a mesh structure, the polymer matrix being formed of the cured photo-crosslinking agent;

inorganic particles distributed in the polymer matrix; and

a lithium salt and an organic solvent impregnated between the polymer matrix and the inorganic particles.

2. The method of claim 1 , wherein the electrolyte paste is coated on the substrate in a thickness ranging from 10 nm to 500 μm.

3. The method of claim 1 , wherein the liquid electrolyte and the photo-crosslinking agent are mixed in a weight ratio of liquid electrolyte to photo-crosslinking agent ranging from 50:50 to 99:1.

4. The method of claim 1 , wherein the liquid electrolyte containing the photo-crosslinking agent and the inorganic particles are mixed in a weight ratio of liquid electrolyte and photo-crosslinking agent to inorganic particles ranging from 10:90 to 90:10.

5. The method of claim 1 , wherein the electrolyte paste has a viscosity ranging from 100 to 10,000 poise under a shear rate condition of 1 sec −1 so that the method controls fluidity of the electrolyte paste.

6. The method of claim 1 , wherein the photo-crosslinking agent comprises at least one of polyethyleneglycol diacrylate, triethyleneglycol diacrylate, trimethylolpropaneethoxylate triacrylate, or Bisphenol A ethoxylate dimethacrylate.

7. The method of claim 1 , wherein the inorganic particles comprise at least one of silicon dioxide (SiO 2 ), aluminum oxide (Al 2 O 3 ), titanium dioxide (TiO 2 ), titanium barium oxide (BaTiO 3 ), lithium oxide (Li 2 O), lithium fluoride (LiF), lithium hydroxide (LiOH), lithium nitride (Li 3 N), barium oxide (BaO), sodium oxide (Na 2 O), lithium carbonate (Li 2 CO 3 ), calcium carbonate (CaCO 3 ), lithium aluminate (LiAlO 2 ), titanium strontium oxide (SrTiO 3 ), tin oxide (SnO 2 ), cerium oxide (CeO 2 ), magnesium oxide (MgO), nickel oxide (NiO), calcium oxide (CaO), zinc oxide (ZnO), zinc peroxide (ZrO 2 ), or silicon carbide (SiC).

8. The method of claim 1 , wherein a mean diameter of the inorganic particles ranges from about 1 nm to about 10 μm.

9. The method of claim 1 , wherein the lithium salt comprises at least one of lithium hexafluorophosphate (LiPF 6 ), lithium tetrafluoroborate (LiBF 4 ), lithium hexafluoroantimonate (LiSbF 6 ), lithium hexafluoroarsenate (LiAsF 6 ), lithium difluoromethanesulfonate (LiC 4 F 9 SO 3 ), lithium perchlorate (LiClO 4 ), lithium aluminate (LiAlO 2 ), lithium tetrachloroaluminate (LiAlCl 4 ), lithium chloride (LiCl), lithium iodide (LiI), lithium bis(oxalato)borate (LiB(C 2 O 4 ) 2 ), lithium trifluoromethanesulfonyl imide (LiN(C x F 2x+1 SO 2 )(C y F 2y+1 SO 2 , where x and y are natural numbers.

10. The method of claim 9 , wherein the organic solvent comprises at least one of ethylene carbonate, propylene carbonate, g-butylrolactone, or ethylene glycol dimethyl ether.

11. The method of claim 1 , wherein the organic solvent comprises at least one of ethylene carbonate, propylene carbonate, g-butylrolactone, or ethylene glycol dimethyl ether.

12. The method of claim 1 , wherein the solid polymeric electrolyte comprises a first portion, a second portion, and a third portion connecting the first and second portions, and one of the first, second, and third portions is located apart from a flat plane connecting the other portions.