Apparatus and method for edge sealing of foam boards
A method and machine for sealing at least one cut edge of a foam board is disclosed. The foam board has a top surface, a bottom surface and at least one cut edge extending between the top surface and the bottom surface. The cut edge is passed over a heated roller to soften the edge and then passed over a second roller having a temperature that is lower than the temperature of the first roller which seals the edge. The cut edge may be milled to square the edge relative to the top and bottom of the board before the cut edge is passed over the heated roller. Additional pairs of rollers may be provided to seal the top surface and the bottom surface of the foam board.
1. A method of sealing at least one cut edge of a foam board, the foam board having a top surface, a bottom surface and the at least one cut edge extending between the top surface and the bottom surface, the at least one cut edge having open cells, the method comprising:
passing the foam board between a first pair of rollers at a speed of 90 ft/min to 120 ft/min, at least one roller in the first pair of rollers having a temperature of 300° F. to 495° F. and engaging the at least one cut edge to soften the at least one cut edge; and
then passing the foam board between a second pair of rollers having a temperature that is lower than the temperature of the at least one roller in the first pair of rollers causing the open cells to become closed.
2. The method of claim 1 also comprising milling the at least one cut edge such that the at least one cut edge is perpendicular to the top surface and perpendicular to the bottom surface of the foam board prior to passing the at least one cut edge over the first roller.
3. The method of claim 1 wherein the foam board is of free foam.
4. The method of claim 1 wherein the foam board is comprised of cells and none of the cells has a diameter greater than 0.26 mm.
5. The method of claim 1 wherein the foam board is a thermoplastic.
6. The method of claim 1 wherein the foam board is polyvinyl chloride, low density polyethylene, high density polyethylene or polypropylene.
7. The method of claim 1 also comprising:
passing the foam board between a third pair of spaced apart rollers, at least one roller in the third pair of rollers having a temperature of 300° F. to 495° F., at a first speed of 90 ft/min to 120 ft/min so that the top surface and the bottom surface engage a respective one roller of the third pair of rollers; and
then passing the foam board between a fourth pair of spaced apart rollers having a temperature that is lower than the temperature of the at least one roller in the third pair of rollers so that the top surface and the bottom surface engage a respective one roller of the fourth pair of rollers.
8. The method of claim 1 also comprising imprinting an indicia on at least one of the cut edges after that edge has passed over the first pair of rollers.
9. The method of claim 1 also comprising milling the at least one of the longitudinal cut edges such that the at least one longitudinal cut edge is perpendicular to the top surface and perpendicular to the bottom surface of the foam board prior to passing the foam board between a first pair of spaced apart rollers.
10. The method of claim 1 wherein the temperature of the at least one roller in the first set of rollers is above a glass transition temperature of the foam board.
11. The method of claim 10 wherein the temperature of the second set of rollers is between 120° F. and 160° F.