Acrylate-styrene-acrylonitrile resin composition having thermochromic resistance at high temperatures
An acrylate-aromatic vinyl-vinyl cyanide resin composition having thermochromic resistance at high temperatures is provided. The resin composition includes: (A) about 20 to about 50% by weight of acrylic graft copolymer; (B) about 20 to about 50% by weight of two types of aromatic vinyl-vinyl cyanide copolymers with different molecular weights; and (C) about 30 to about 50% by weight of alpha-methyl styrene terpolymer.
1. An acrylate-aromatic vinyl-vinyl cyanide resin composition with thermochromic resistance at high temperature, comprising:
(A) about 20 to about 50% by weight of acrylic graft copolymer,
(B) about 30 to about 50% by weight of two types of aromatic vinyl-vinyl cyanide copolymers having different molecular weights, and
(C) about 30 to about 50% by weight of alpha-methyl styrene terpolymer, wherein said alpha-methyl styrene terpolymer (C) is a vinyl cyanide compound-styrene-alpha-methyl styrene terpolymer and comprises about 20 to about 40% by weight of vinyl cyanide compound, about 15 to about 30% by weight of styrene monomer, and about 40 to about 65% by weight of alpha-methyl styrene.
2. The resin composition of claim 1 , wherein said acrylic graft copolymer (A) comprises about 40 to about 60% by weight acrylic rubber and about 40 to about 60% by weight of monomer compounds including aromatic vinyl compound and vinyl cyanide compound.
3. The resin composition of claim 2 , wherein the monomer compounds including vinyl cyanide compound and aromatic vinyl mixture comprises about 20 to about 30% by weight of vinyl cyanide compound and about 70 to about 80% by weight of aromatic vinyl compound.
4. The resin composition of claim 2 , wherein the acrylic rubber comprises a C2 to C10 alkyl acrylate and has an average rubber particle size of about 0.1 to about 0.5 μm.
5. The resin composition of claim 2 , wherein said aromatic vinyl compound comprises styrene, alpha-methylstyrene, p-methylstyrene, p-t-butylstyrene, 2,4-dimethylstyrene, chlorostyrene, vinyltoluene, vinylnaphthalene, or a combination thereof.
6. The resin composition of claim 2 , wherein said vinyl cyanide compound comprises acrylonitrile, methacrylonitrile, or a combination thereof.
7. The resin composition of claim 1 , wherein said acrylic graft copolymer (A) is acrylonitrile-styrene-acrylate (ASA) graft copolymer.
8. The resin composition of claim 1 , wherein the two types of aromatic vinyl-vinyl cyanide copolymers (B) comprise about 20 to about 35% by weight of vinyl cyanide compound and about 65 to about 80% by weight of aromatic vinyl compound.
9. The resin composition of claim 8 , wherein said aromatic vinyl-vinyl cyanide copolymer (B) comprises (b1) a high molecular weight aromatic vinyl-vinyl cyanide copolymer having a weight average molecular weight (Mw) of about 130,000 to about 150,000 and (b2) a low molecular weight aromatic vinyl-vinyl cyanide copolymer having a average molecular weight (Mw) of about 80,000 to about 100,000.
10. The resin composition of claim 8 , wherein said aromatic vinyl compound comprises styrene, alpha-methylstyrene, p-methylstyrene, p-t-butylstyrene, 2,4-dimethylstyrene, chlorostyrene, vinyltoluene, vinylnaphthalene, or a combination thereof, and said vinyl cyanide compound comprises acrylonitrile, methacrylonitrile, or a combination thereof.
11. The resin composition of claim 1 , further comprising about 5 to about 10 parts by weight of a maleimide heat resistant copolymer (D), based on about 100 parts by weight of a base resin comprising said acrylic graft copolymer (A), aromatic vinyl-vinyl cyanide copolymer (B) and alpha-methyl styrene terpolymer (C).
12. The resin composition of claim 11 , wherein said maleimide heat resistant copolymer comprises a copolymer comprising aromatic vinyl monomer, vinyl cyanide monomer, and N-substituted maleimide monomer.
13. The resin composition of claim 1 , wherein the composition has a change in yellowness value (ΔYI) of less than about 7.0 measured using a spectrocolorimeter in accordance with ASTMD-1925, wherein the yellowness value of a specimen of the composition is measured before and after the specimen is maintained at a temperature of 250° C. for 10 min., wherein the specimen has a thickness of 2.2 mm, a width of 10 mm, and a length of 6 mm prepared at a forming temperature of 250° C., a mold temperature of 70° C., and a cooling time of 300 seconds.
14. An acrylate-aromatic vinyl-vinyl cyanide resin composition with thermochromic resistance at high temperature, comprising:
(A) about 20 to about 50% by weight of acrylic graft copolymer,
(B) about 30 to about 50% by weight of two types of aromatic vinyl-vinyl cyanide copolymers having different molecular weights, and
(C) about 30 to about 50% by weight of alpha-methyl styrene terpolymer, and
(D) about 5 to about 10 parts by weight of a maleimide heat resistant copolymer (D), based on about 100 parts by weight of a base resin comprising said acrylic graft copolymer (A), aromatic vinyl-vinyl cyanide copolymer (B) and alpha-methyl styrene terpolymer (C), wherein said maleimide heat resistant copolymer comprises a copolymer comprising aromatic vinyl monomer, vinyl cyanide monomer, and N-substituted maleimide monomer.