Provided is a microporous separator for a lithium secondary battery having shutdown properties wherein the separator comprises a propylene random copolymer which has a melt index of 0.5-10 g/10 minutes and comprises one or more species of comonomers in the content of 0.1-8 wt %.
1. A microporous separator for a lithium secondary battery having a shutdown function consisting of a microporous monolayer film, consisting of a propylene random copolymer resin,
wherein the propylene random copolymer has a melt index of 0.5-10 g/10 minutes at 230° C. and under a load of 2.16 kg and comprises one or more comonomers in the amount of 0.1 to 8 wt % of the propylene random copolymer, and
wherein the microporous separator exerts a shutdown function at the temperature of 137° C. or less.
2. The microporous separator according to claim 1 , which has a thickness of 1-100 μm and a porosity of 20-99%.
3. The microporous separator according to claim 1 , which is prepared via the processes of extrusion in the form of a non-porous film, annealing and elongation at 20-25° C. and then at 90-150° C.