Nanofilaments of catalytic materials for chemical process improvements
A Fischer-Tropsch process including the steps of providing a reactor having a substrate element with a surface and a plurality of elongated micro-structures of catalyst material attached to the substrate surface The catalyst material includes at least one of cobalt, iron, or ruthenium and the micro-structures have a width of less than about 1 um and a length at least five times the width. A carbon compound and hydrogen are injected into the reactor such that at least a portion of the carbon compound and hydrogen contact the catalyst material. The carbon compound and hydrogen are reacted with the catalyst at a temperature between about 150° F. and about 400° F.
1. A Fischer-Tropsch process comprising the steps of:
(a) providing a reactor including substrate elements having catalyst filaments formed on the substrates elements, the catalyst filaments comprising (i) a diameter of about 10 nm to about 500 nm; (ii) a length of about 30 nm to about 5000 nm; (iii) a packing density of between 5 mg/cm 2 and about 200 mg/cm 2 ; and (iv) being formed either of cobalt, iron, or ruthenium;
(b) injecting a carbon compound and hydrogen into the reactor such that at least a portion of the carbon compound and hydrogen contact the catalyst filaments;
(c) reacting the carbon compound and hydrogen with the catalyst filaments at a temperature of between about 150° F. and about 400° F. and a pressure of less than about 400 psig.
2. The process according to claim 1 , wherein the substrate elements are substantially nonporous.
3. The process according to claim 1 , wherein the filaments packing density is at least about 20 mg/cm 2 .
4. The process according to claim 1 , wherein the substrate elements are formed of a conductive material.
5. The process according to claim 1 , wherein the substrate elements are a nonconductive material with a layer of conductive material applied thereto.
6. The process according to claim 1 , wherein the reaction pressure is less than about 250 psig.
7. The process according to claim 1 , wherein the reaction pressure is less than about 100 psig and the reaction temperature is between about 200° F. and about 300° F.
8. The process according to claim 1 , wherein the catalyst filaments have a diameter between about 10 nm to about 200 nm.
9. The process according to claim 1 , wherein the catalyst filaments are formed through a process comprising the steps of:
(a) forming an aluminum layer ranging from about 300 nm to about 2000 nm in depth on the substrate elements;
(b) anodizing the aluminum layer until at least about 85% percent by weight of the aluminum layer is converted to an aluminum oxide (AAO) layer;
(c) forming the filaments on the substrate elements by pulse reverse electroplating.
10. The process according to claim 9 , wherein the pulse reverse electroplating includes a current density of about 1 mA/cm 2 to 200 mA/cm 2 , a forward time of about 1 ms to 500 ms, a reverse time of about 1 ms to 500 ms, and a rest period of about 10 ms to 2,000 ms.