Fiber composition comprising 1,3-glucan and a method of preparing same
View Patent ↗The present invention is a solution comprising poly(α(1→3) glucan) and an ionic liquid. The solution can further contain a non-solvent that is water or an ionic liquid. The solution is suitable for use as a spinning solution for the preparation of fibers of poly(α(1→3) glucan) without the requirement of first derivatizing the poly(α(1→3) glucan).
1. A solution comprising poly(α(1→3) glucan) and an ionic liquid selected from the group consisting of 1-ethyl, 3-methyl imidazolium acetate; 1-butyl, 3-methyl imidazolium chloride, 1-hexyl, 3-methyl imidazolium chloride, and a mixture of 1-ethyl, 3-methyl imidazolium acetate and 1-butyl, 3-methyl imidazolium acetate.
2. The solution of claim 1 wherein the ionic liquid is 1-ethyl, 3-methyl imidazolium acetate.
3. The solution of claim 1 further comprising a concentration of non-solvent up to 30% on a weight basis of the total weight of solvent plus non-solvent.
4. The solution of claim 1 wherein the poly(α(1→3) glucan) is present at a solids content of from about 5 weight percent to about 20 weight-%.
5. A process for spinning a fiber from a solution of poly(α(1→3) glucan) in an ionic liquid, the process comprising the steps:
a) forming a mixture by combining (i) an ionic liquid selected from the group consisting of 1-ethyl, 3-methyl imidazolium acetate; 1-butyl, 3-methyl imidazolium chloride, 1-hexyl, 3-methyl imidazolium chloride, and a mixture of 1-ethyl, 3-imidazolium acetate and 1-butyl, 3-methyl imidazolium acetate; and, (ii) poly(α(1→3) glucan); said solution having a solids content of 5 to 25% by weight;
b) heating said mixture under agitation to a temperature below the boiling point of the ionic liquid to obtain a glucan spinning solution;
c) causing said spinning solution to flow through a spinneret, thereby forming a fibrous strand;
d) causing said fibrous strand to contact a coagulating liquid characterized by a pH in the range of 1 to 7, thereby forming a poly(α(1→3) glucan) fiber.
6. The process of claim 5 wherein the ionic liquid is 1-ethyl, 3-methyl imidazolium acetate.
7. The process of claim 5 wherein the solution further comprises up to 30 weight percent of a non-solvent that is water or an ionic liquid, on the basis of the total weight of solvent plus non-solvent.
8. The process of claim 5 wherein the poly(α(1→3) glucan) is present in the solution at a solids content of from about 5 weight percent to about 20 weight-%.
9. The process of claim 5 wherein the coagulating liquid is glacial acetic acid.