Mechanically-activated shape memory polymer spinal cage
View Patent ↗Provided herein are shape memory polymer spinal cages including polymers with intended deployment at temperatures far below the onset of the glassy transition of the shape memory polymer. The described shape memory polymer spinal cages are adapted to be deployed by mechanical activation rather than thermal activation or activation by other stimuli. Thus, the shape memory polymers used herein are configured to have transition temperatures far above their temperatures of intended use, thereby requiring mechanical activation to recover stored strains.
1. A spinal cage system, comprising:
a body made of a shape memory polymer with a stored strain, wherein the shape memory polymer has a transition onset temperature above 120 degrees Fahrenheit;
wherein the stored strain comprises a difference in shape between an insertion shape of the body having an insertion axis and a deployed shape of the body adapted to cover a central intervertebral space;
a detachable deployment mechanism that connects with the body along the insertion axis at an insertion-leading portion of the body and at an insertion-trailing portion of the body;
wherein the deployment mechanism is adapted to activate recovery within a plurality of portions of the shape memory polymer only with mechanical forces applied along the insertion axis between the insertion-leading portion and the insertion trailing portion; and
wherein the shape memory polymer is adapted to expand via only thermal expansion below 120 degrees Fahrenheit and without undergoing any shape memory polymer activation.
2. The spinal cage system of claim 1 , wherein the deployment mechanism provides mechanical forces without any thermal energy input to the shape memory polymer.
3. The spinal cage system of claim 1 , wherein the body contains a stored strain that was set below 120 degrees Fahrenheit.
4. The spinal cage system of claim 1 , wherein the deployed shape of the body is in the form of a loop and comprises a ventral portion of the loop and a dorsal portion of the loop, and wherein the insertion shape of the body has the ventral portion and the dorsal portion collapsed toward the insertion axis.
5. The spinal cage system of claim 1 , wherein the insertion axis is 35 degrees with respect to the sagittal plane.
6. The spinal cage system of claim 1 , wherein the stored strain does not activate over the period of 1 year while packaged at a temperature below 120 degrees Fahrenheit.
7. A method comprising:
shaping a spinal cage from a shape memory polymer with a transition temperature above 120 degrees Fahrenheit;
imparting a stored strain on the shape memory polymer;
forming holes in a vertical wall of the spinal cage along an insertion axis of the spinal cage, the holes adapted to receive a deployment mechanism adapted to provide deployment forces along the insertion axis to activate recovery of the stored strain in the spinal cage; and
storing the spinal cage with the stored strain in a sterile package below 120 degrees Fahrenheit.
8. The method of claim 7 , wherein the imparting is performed while the shape memory polymer is below 120 degrees Fahrenheit.
9. The method of claim 7 , wherein a transition onset temperature of the shape memory polymer is above 120 degrees Fahrenheit.
10. The method of claim 7 , wherein the imparting is performed including:
heating the shape memory polymer to a temperature at or above the transition temperature;
while the shape memory polymer is at or above the transition temperature, straining the shape memory polymer with the stored strain; and
while maintaining the stored strain in the shape memory polymer, cooling the shape memory polymer to below the transition temperature.
11. The method of claim 7 , wherein the imparting is performed via straining the shape memory polymer with the stored strain while the shape memory polymer is maintained at a temperature below the transition temperature of the shape memory polymer.
12. The method of claim 7 , wherein the imparting is performed via straining the shape memory polymer with the stored strain while a modulus of the shape memory polymer is above 2.5 gigapascals (GPa).
13. The method of claim 7 , wherein the forming is performed while the shape memory polymer has a modulus above 2.5 gigapascals (GPa).
14. The method of claim 7 , wherein the forming is performed after imparting the stored strain on the shape memory polymer.
15. The method of claim 14 , wherein the forming is performed by cutting slots in the vertical wall perpendicular to the insertion axis.
16. The method of claim 7 , further comprising:
storing the spinal cage with the deployment mechanism in the sterile package.
17. A method comprising:
receiving a spinal cage formed of a shape memory polymer with a transition onset temperature above 120 degrees Fahrenheit and containing a stored strain defining a difference between an expanded shape and an insertion shape;
inserting the spinal cage in the insertion shape into an intervertebral space along an insertion axis of the spinal cage;
engaging a deployment mechanism with the spinal cage to apply a deployment force to the spinal cage along the insertion axis;
applying the deployment force to the spinal cage along the insertion axis to activate the shape memory polymer to recover the stored strain while the shape memory polymer remains below the transition onset temperature;
wherein the applying the deployment force is performed with the shape memory polymer being below the transition onset temperature; and
removing the deployment mechanism from the spinal cage in the expanded shape while the shape memory polymer is below the transition onset temperature.
18. The method of claim 17 , wherein the inserting step is performed with an insertion tool that contains the deployment mechanism and wherein the engaging step is performed before the inserting step.
19. The method of claim 17 , further comprising:
determining from an indication from the deployment mechanism that at least a portion of the spinal cage has completed recovery of all strain stored in the portion of the spinal cage;
wherein the removing is performed in response to the determining step.
20. The method of claim 17 , wherein the expanded shape covers a majority of an intervertebral space and wherein the insertion shape comprises a cross-section of less than about 1 cm by 1 cm when measured perpendicular to the insertion axis of the spinal cage.