Polyolefin compositions for film, fiber and molded articles
View Patent ↗Polyolefin compositions prepared by processing a polyolefin resin and a mixture of a select hindered phenol and select liquid phosphite above the melting point of the polyolefin contain a higher amount of retained active phosphorus than when other common phosphites are used. The compositions, and films, fibers and other molded articles prepared from the compositions show improved stabilization against NOX discoloration and long term oxidation. The select liquid phosphite consists mainly of a mixture of triphenyl phosphite derivatives wherein the phenyl groups are substituted by different numbers of butyl and/or amyl substituents.
1. A stabilized polyolefin composition for film or fiber formation prepared by processing a mixture comprising a polyolefin and antioxidant composition at temperatures above the melting point of the polyolefin,
wherein the antioxidant composition comprises a combination of hindered phenol and liquid phosphite in a weight ratio of hindered phenol to phosphite of about 1:1 to about 1:10 and is present in said mixture before processing at a concentration of from about 0.01 wt % to about 8 wt %, based on the combined weight of polyolefin plus antioxidant composition,
and wherein after processing at temperatures above the melting point of the polyolefin the stabilized polyolefin composition comprises greater than 30% retained active phosphorus based on the active phosphorus of the mixture comprising the polyolefin and antioxidant composition prior to processing, wherein said phenol is selected from the group consisting of compounds of formula I
wherein R 1 is C 1-18 alkyl, C 5-12 cyclic alkyl, phenyl, styryl, cumyl or H, R 2 is C 1-18 alkyl, C 5-12 cyclic alkyl, phenyl, styryl, cumyl, or a group
wherein R and R′ are independently selected from H, methyl, ethyl or propyl, R 3 is C 1-18 alkyl, C 5-12 cyclic alkyl, styryl, cumyl, H or a group
—CH 2 CH 2 COOR″
wherein R″ is a C 1-18 alkyl or a group
wherein 1, 2 or 3 G groups are 3,5-bis(1,1-dimethylethyl)-4-hydroxy-benzenepropanoyl and the remaining G groups are independently H or C 1-4 alkyl;
and said liquid phosphite comprises a mixture consisting of:
from 0 to 20 weight percent based on the total weight of phosphite of a tris(diamylphenyl)phosphite or tris(dibutylphenyl)phosphite;
from 20 to 75 weight percent based on the total weight of the phosphite of a tris(monoamylphenyl)phosphite or tris(monobutylphenyl)phosphite;
from 2 to 20 weight percent based on the total weight of the phosphite of a bis(diamylphenyl)monoamylphenyl phosphite or a bis(dibutylphenyl)monobutylphenyl phosphite;
and from 15 to 60 weight percent based on the total weight of the phosphite of a bis(monoamylphenyl)diamylphenyl phosphite or a bis(monobutylphenyl)dibutylphenyl phosphite,
which liquid phosphite makes up at least 90% by weight of all phosphites present in the composition before processing.
2. The composition according to claim 1 wherein the phenol is a compound of formula I wherein R 1 and R 2 are independently selected from C 1-4 alkyl, and R 3 is C 1-8 alkyl or a group
—CH 2 CH 2 COOR″,
wherein R″ is a C 1-18 alkyl or a group
wherein each group G is 3,5-bis(1,1-dimethylethyl)-4-hydroxy-benzenepropanoyl.
3. A film or fiber prepared from a composition according to claim 1 .
4. The composition according to claim 2 wherein said liquid phosphite comprises a mixture consisting of:
from 0 to 20 weight percent based on the total weight of phosphite of tris(di-t-amylphenyl)phosphite;
from 20 to 70 weight percent based on the total weight of the phosphite of tris(mono-t-amylphenyl)phosphite;
from 2 to 20 weight percent based on the total weight of the phosphite of bis(di-t-amylphenyl)mono-t-amylphenyl phosphite; and
from 15 to 60 weight percent based on the total weight of the phosphite of a bis(mono-t-amylphenyl)di-t-amylphenyl phosphite,
which mixture which is liquid at 25.degree. C. makes up at least 90% by weight of all phosphites present in the composition.
5. The composition according to claim 2 wherein said liquid phosphite comprises a mixture consisting of:
from 0 to 3 weight percent based on the total weight of phosphite of tris(di-t-butylphenyl)phosphite;
from 35 to 75 weight percent based on the total weight of the phosphite of tris(mono-t-butylphenyl)phosphite;
from 5 to 15 weight percent based on the total weight of the phosphite of bis(di-t-butylphenyl)monobutylphenyl phosphite; and
from 21 to 47 weight percent based on the total weight of the phosphite of bis(mono-t-butylphenyl)dibutylphenyl phosphite,
which mixture which is liquid at 25.degree. C. makes up at least 90% by weight of all phosphites present in the composition.
6. A film or fiber prepared from a composition according to claim 4 .
7. A film or fiber prepared from a composition according to claim 5 .
8. The stabilized composition of claim 1 wherein the polyolefin is a polyethylene polymer or copolymer.
9. The stabilized composition of claim 2 wherein the polyolefin is a polyethylene polymer or copolymer.
10. The film of claim 3 wherein the polyolefin in the composition is a polyethylene polymer or copolymer.
11. The film of claim 6 wherein the polyolefin in the composition is a polyethylene polymer or copolymer.
12. The film of claim 7 wherein the polyolefin in the composition is a polyethylene polymer or copolymer.