BORON-SILICON-CARBON CERAMIC MATERIALS AND METHOD OF MAKING
A reaction bonded ceramic body that has 50% to 60%, by weight, boron carbide, and 20% to 30%, by weight, silicon carbide. The reaction bonded ceramic body has least a portion of the boron carbide reacted with silicon to become siliconized boron carbide. Also, a method of making a reaction bonded ceramic material. The method may include the steps of forming a green body from a mixture of boron carbide, carbon, and an organic binder, and contacting the green body with a liquid infiltrant comprising silicon. The infiltrant has a temperature of about 1625° C. to about 1700° C. Furthermore, a method of making a reaction bonded boron carbide ceramic body. The method includes the steps of forming a green body from a mixture of boron carbide, carbon, and an organic binder. The weight ratio of boron carbide to carbon in the green body may be about 5:5 to 1 or more. The method also includes siliconizing a first portion of the boron carbide to siliconized boron carbide by contacting the green body with a molten silicon infiltrant, where the infiltrant has a temperature of about 1625° C. to about 1700° C. The method may further include dissolving a second portion of the boron carbide in the silicon infiltrant, where at least some of the dissolved boron carbide is reprecipated as smooth particulates.
1 . A method of making a reaction bonded ceramic material, the method comprising:
forming a green body from a mixture of boron carbide, carbon, and an organic binder;
contacting the green body with a infiltrant comprising silicon and boron, wherein a concentration of the boron in the infiltrant is not so high to prevent reaction between the silicon in the infiltrant and the boron carbide in the green body, and wherein the infiltrant has a temperature of about 1625° C. to about 1700° C.; and
dissolving a portion of the boron carbide in the silicon and boron infiltrant to form a liquid silicon and boron solution, wherein at least a portion of the dissolved boron carbide reacts with the silicon and boron infiltrant in the solution, and wherein the solution precipitates needle-shaped structures of silicon carbide when cooled.
2 . The method of claim 1 , wherein the infiltrant contacts the green body in a low-pressure atmosphere having a pressure of about 100 mTorr or less.
3 . The method of claim 1 , wherein the green body comprises:
80% to 90%, by weight, boron carbide;
10% to 20%, by weight, free carbon.
4 . The method of claim 3 , wherein the free carbon comprises an organic binder.
5 . The method of claim 3 , wherein the free carbon comprises graphite.
6 . A method of making a reaction bonded boron carbide ceramic body, the method comprising:
forming a green body from a mixture of boron carbide, carbon, and an organic binder, wherein the weight ratio of boron carbide to carbon in the green body is about 5:5 to 1 or more;
siliconizing a first portion of the boron carbide to siliconized boron carbide by contacting the green body with a silicon and boron infiltrant, wherein a concentration of the boron in the infiltrant is not so high to prevent reaction between the silicon in the infiltrant and the boron carbide in the green body, and wherein the infiltrant has a temperature of about 1625° C. to about 1700° C.; and
dissolving a second portion of the boron carbide in the silicon and boron infiltrant to form a liquid silicon and boron solution, wherein at least some of the dissolved boron carbide reacts with the silicon and boron infiltrant in the solution, and wherein the solution precipitates needle-shaped structures of silicon carbide when cooled.
7 . The method of claim 6 , wherein the siliconzed boron carbide comprises B 12 C 2 Si, wherein a silicon atom replaces one of the carbon atoms in the carbon backbone of the boron carbide.
8 . The method of claim 7 , wherein the silicon atom replaces a middle carbon atom in the carbon backbone.
9 . The method of claim 6 , wherein the siliconzed boron carbide comprises B 12 CSi 2 , wherein two silicon atoms replace two carbon atoms in the carbon backbone of boron carbide.
10 . The method of claim 6 , wherein the smooth particulates of reprecipitated boron carbide lack a sharp edge.
11 . The method of claim 6 , wherein the smooth particulates of reprecipitated boron carbide are substantially spherical.
12 . The method of claim 6 , wherein the green body comprises about 85%, by wt., boron carbide and about 15%, by wt., carbon.
13 . The method of claim 6 , wherein the reaction bonded boron carbide ceramic body comprises less than 10%, by wt., unsiliconized boron carbide.
14 . The method of claim 6 , wherein the reaction bonded boron carbide ceramic body comprises more than 10%, by wt., silicon.
15 . The method of claim 6 , wherein the reaction bonded boron carbide ceramic body comprises more than 20%, by wt., silicon carbide.
16 . The method of claim 15 , wherein at least a portion of the silicon carbide is β-SiC.
17 . The method of claim 6 , wherein the reaction bonded boron carbide ceramic body comprises:
about 9.3%, by wt., unsiliconized boron carbide;
about 22.5%, by wt., silicon carbide; and
about 10.9%, by wt., silicon metal.
18 . The method of claim 1 , wherein the boron in the infiltrant comes from elemental boron or boron carbide.
19 . The method of claim 6 , wherein the boron in the infiltrant comes from elemental boron or boron carbide.