Highly insulating polyurethane foam and method for manufacturing same
The rigid polyurethane foam includes thermally expandable fine particles disposed between two or more adjacent cells, so as to be exposed to the inside and/or the outside of a unit cell, and a filler which is dispersed on the surface of the thermally expandable fine particles and/or on the inner and/or outer surfaces of the unit cell. The cells of the rigid polyurethane foam can be small and uniform in size and can be highly insulating.
1. A rigid polyurethane foam comprising unit cells, comprising: thermally expandable fine particles placed between at least two adjacent unit cells to penetrate into a unit cell, to be exposed from a unit cell, or both, and a filler dispersed on surfaces of the thermally expandable fine particles, on inner surfaces of the unit cells, on outer surfaces of the unit cells, or on a combination thereof,
wherein the cells have an average diameter of about 200 μm to about 300 μm and the rigid polyurethane foam has a cell close ratio of about 85% to about 99%.
2. The rigid polyurethane foam according to claim 1 , wherein the unit cells include a strut forming a cell frame, a cell wall, and a cell vertex, and wherein the thermally expandable fine particles are formed to penetrate a strut, cell wall, cell vertex, or a combination thereof of a unit cell.
3. The rigid polyurethane foam according to claim 1 , wherein the thermally expandable fine particles have a hollow structure.
4. The rigid polyurethane foam according to claim 1 , wherein the thermally expandable fine particles are present in an amount of about 0.5 parts by weight to about 10 parts by weight based on 100 parts by weight of a urethane resin forming the polyurethane foam.
5. The rigid polyurethane foam according to claim 1 , wherein the thermally expandable fine particles have a mean volume diameter of about 5 μm to about 40 μm before being foamed.
6. The rigid polyurethane foam according to claim 1 , wherein the thermally expandable fine particles have an encapsulated structure obtained by encapsulation of a hydrocarbon-based foamable compound by a polymer shell, the hydrocarbon-based foamable compound having a boiling point of about −10° C. to about 50° C., and a polymer material constituting the polymer shell has a glass transition temperature of about 40° C. to about 100° C.
7. The rigid polyurethane foam according to claim 1 , wherein the filler has an average particle diameter of about 0.01 μm to about 50 μm.
8. The rigid polyurethane foam according to claim 1 , wherein the filler comprises at least one of carbon black, graphite, carbon nanotubes, carbon fibers, titanium dioxide, silica, and clay.
9. The rigid polyurethane foam according to claim 1 , wherein the filler is present in an amount of about 0.1 parts by weight to about 10 parts by weight based on 100 parts by weight of a polyol.
10. The rigid polyurethane foam according to claim 1 , wherein the cells are formed by foaming with a blowing agent.
11. The rigid polyurethane foam according to claim 10 , wherein the blowing agent and the thermally expandable fine particles are present in a weight ratio of about 1:0.2˜2.
12. The rigid polyurethane foam according to claim 11 , wherein the blowing agent comprises at least one of C 5 -C 6 hydrocarbons, dialkyl ethers, alkyl alkanoates, halogenated hydrocarbons, acetone, and water.
13. The rigid polyurethane foam according to claim 1 , wherein the rigid polyurethane foam has a foam density of about 20 g/cm 3 to about 40 g/cm 3 and a thermal conductivity (K-factor) of about 145×10 −4 kcal/m·h·° C. to about 165×10 −4 kcal/m·h·° C. according to ASTM-C518.
14. The rigid polyurethane foam according to claim 1 , wherein the rigid polyurethane foam has a foam density of about 30 g/cm 3 to about 37 g/cm 3 , a thermal conductivity (K-factor) of about 155×10 −4 kcal/m·h·° C. to about 163×10 −4 kcal/m·h·° C. according to ASTM-C518, and a cell close ratio of about 90% to about 99%.
15. A method for manufacturing rigid polyurethane foam, comprising:
preparing a dispersion liquid by dispersing thermally expandable fine particles and a filler in a premixed polyol;
adding a blowing agent to the dispersion liquid; and
forming rigid polyurethane foam by reacting an isocyanate with the dispersion liquid containing the blowing agent, and foaming the reactant with heat of urethane reaction, wherein the blowing agent and the thermally expandable fine particles are present in a weight ratio of about 1:0.2˜2,
wherein the cells have an average diameter of about 200 μm to about 300 μm and the rigid polyurethane foam has a cell close ratio of about 85% to about 99%.
16. The method according to claim 15 , wherein the premixed polyol comprises a polyol, a dispersant, a catalyst, and water.
17. The method according to claim 15 , wherein the thermally expandable fine particles have a mean volume diameter of about 5 μm to about 40 μm before being foamed.
18. The method according to claim 15 , wherein the filler is present in an amount of about 0.1 parts by weight to about 10 parts by weight based on 100 parts by weight of a polyol.
19. The method according to claim 15 , wherein the isocyanate is added in an amount of about 90 parts by weight to about 200 parts by weight based on 100 parts by weight of the polyol.