Cement compositions including resilient graphitic carbon fraction
View Patent ↗A method for improving the thermal characteristics of cement compositions is provided in which fine resilient graphitic carbon particles (“RGC”) are substituted for a portion of the fine aggregate (typically sand) in the cement formulation. For the purposes of the present disclosure, “fine” is intended to describe particulates having a mesh size of less than about 8 mesh, or a particle size of less than about 2.38 mm, or, more preferably when referring to RGC, a mesh size of less than about 16 mesh and a particle size of less than about 1.19 mm. “Resilient” is intended to describe graphitic carbon particles that exhibit a rebound of at least about 20% after compression to 10,000 psi.
1. A concrete composition comprising a fine fraction that is partially or entirely resilient graphitic carbon particles having a mesh size of less than about 8 mesh (−2.38 mm) and exhibiting a rebound of at least about 20% after compression to 10,000 psi, wherein the resilient graphitic carbon particles are selected from synthetic graphite, thermally treated calcined petroleum coke, and a combination synthetic graphite and thermally treated calcined petroleum coke, the concrete composition further comprising: 0.5 wt %-32.3. wt % resilient graphitic carbon; 5.2 wt %-71.0 wt % coarse aggregate; 0 wt %-88.6 wt % fine aggregate; and 15.7 wt %-23.2 wt % cement.
2. The concrete composition of claim 1 wherein 3.1 wt %-4.6 wt % fly ash is substituted for an equal amount of the cement portion.
3. The concrete composition of claim 1 wherein the cement comprises one or more of Portland cement formulations ASTM C150 Types I, II, III and V, oil well Portland cements, gypsum-cement blends, fly ash-cement blends, and floor leveling gypsum-based cements.
4. A concrete composition comprising a fine fraction that is partially or entirely resilient graphitic carbon particles having a mesh size of less than about 8 mesh (−2.38 mm) and exhibiting a rebound of at least about 20% after compression to 10,000 psi, wherein the resilient graphitic carbon particles are selected from synthetic graphite, thermally treated calcined petroleum coke, and a combination synthetic graphite and thermally treated calcined petroleum coke, the concrete composition further comprising: 0.5 wt %-39.0 wt % resilient graphitic carbon; 0 wt % coarse aggregate; 21.0 wt %-76.2 wt % fine aggregate; and 23.3 wt %-40.0 wt % cement.
5. The concrete composition of claim 4 wherein 4.7 wt %-8.0 wt % fly ash is substituted for an equal amount of the cement portion.
6. The concrete composition of claim 4 wherein the cement comprises one or more of Portland cement formulations ASTM C150 Types I, II, III and V, oil well Portland cements, gypsum-cement blends, fly ash-cement blends, and floor leveling gypsum-based cements.
7. A method for improving the thermal and electrical characteristics of a concrete composition including a fine aggregate fraction comprising substituting fine resilient graphitic carbon particles for a portion of the fine aggregate such that the concrete has composition in accordance with claim 1 or 4 .
8. The method of claim 7 wherein the fine aggregate and fine resilient graphitic carbon particles have a mesh size of less than about 8 mesh (−2.38 mm).
9. The method of claim 8 wherein the resilient graphitic carbon particles exhibit a rebound of at least about 20% after compression to 10,000 psi.
10. The method of claim 9 wherein the resilient graphitic carbon particles are selected from synthetic graphite, thermally treated calcined petroleum coke, and a combination synthetic graphite and thermally treated calcined petroleum coke.
11. The method of claim 10 wherein the concrete composition to which the resilient graphitic carbon particles is added comprises one or more of Portland cement formulations ASTM C150 Types I, II, III and V, oil well Portland cements, gypsum-cement blends, fly ash-cement blends, and floor leveling gypsum-based cements.