Adhesives for securing optical fibers to ferrules of optical connectors and methods for use thereof
View Patent ↗An optical fiber may be secured to a ferrule of an optical connector with an adhesive mixture. The optical fiber may be secured by preparing an adhesive mixture, disposing the adhesive mixture in a fiber-receiving passage defining an inner surface of the ferrule, inserting the optical fiber into the fiber-receiving passage and into contact with the adhesive mixture, and curing the adhesive mixture. The adhesive mixture may be prepared by forming a base mixture that includes a base solvent, an alkyltrialkoxysilane, an aryltrialkoxysilane, and an aryltrifluorosilane. The adhesive mixture may be cured by heating to a temperature of at least about 200° C. and cooling to room temperature or below.
1. A method for securing an optical fiber to a ferrule of an optical connector, the method comprising:
preparing an adhesive mixture, wherein preparing the adhesive mixture comprises forming a base mixture comprising a base solvent, an alkyltrialkoxysilane, an aryltrialkoxysilane, and an aryltrifluorosilane;
disposing the adhesive mixture in a fiber-receiving passage defining an inner surface of the ferrule;
inserting the optical fiber into the fiber-receiving passage and into contact with the adhesive mixture; and
curing the adhesive mixture by heating to a temperature of at least about 200° C. and cooling the adhesive mixture to room temperature or below.
2. The method of claim 1 , wherein preparing the adhesive mixture further comprises:
heating the base mixture to form a reacted mixture comprising an alcohol;
evaporating at least a portion of the alcohol in the reacted mixture to form a resin; and
mixing a reconstituting solvent with the resin to reconstitute the resin into an adhesive mixture.
3. The method of claim 2 , wherein the reconstituting solvent comprises isopropanol.
4. The method of claim 1 , wherein the curing of the adhesive mixture comprises heating the adhesive mixture to at least about 200° C. in less than about 15 seconds and by cooling the adhesive mixture to room temperature or below in less than about 5 minutes.
5. The method of claim 1 , wherein the curing of the adhesive mixture comprises heating the adhesive mixture by a laser.
6. The method of claim 1 , further comprising pretreating the ferrule with an acid treatment or an oxygen plasma treatment, or both, prior to disposing the adhesive mixture in the fiber receiving passage of the ferrule.
7. The method of claim 1 , further comprising at least partially coating an area of the optical fiber that makes contact with the adhesive mixture with tetraethyl orthosilicate.
8. The method of claim 1 , wherein the base mixture further comprises tetraethyl orthosilicate.
9. The method of claim 1 , wherein the base mixture consists essentially of the alkyltrialkoxysilane, the aryltrialkoxysilane, the aryltrifluorosilane, and one or more base solvents.
10. The method of claim 1 , wherein the base mixture consists essentially of one or more base solvents, the alkyltrialkoxysilane, the aryltrialkoxysilane, the aryltrifluorosilane, and tetraethyl orthosilicate.
11. A method for preparing an adhesive, the method comprising:
forming a base mixture comprising a base solvent, an alkyltrialkoxysilane, an aryltrialkoxysilane, and an aryltrifluorosilane;
heating the base mixture to form a reacted mixture comprising an alcohol;
evaporating at least a portion of the alcohol in the reacted mixture to form a resin; and
mixing a reconstituting solvent with the resin to reconstitute the resin into an adhesive mixture; and
curing the adhesive mixture by heating to a temperature of at least about 200° C. and cooling the adhesive mixture to room temperature or below.
12. The method of claim 11 , wherein the base mixture further comprises tetraethyl orthosilicate.
13. The method of claim 11 , wherein the base mixture consists essentially of the alkyltrialkoxysilane, the aryltrialkoxysilane, the aryltrifluorosilane, and one or more base solvents.
14. The method of claim 13 , wherein the base solvent comprises deionized water.
15. The method of claim 11 , wherein the base mixture consists essentially of the alkyltrialkoxysilane, the aryltrialkoxysilane, the aryltrifluorosilane, tetraethyl orthosilicate, and one or more base solvents.
16. The method of claim 15 , wherein the base solvent comprises deionized water.
17. An optical connector for terminating an optical fiber, the optical connector comprising a ferrule, the optical fiber, and an adhesive, wherein:
the ferrule comprises a fiber-receiving passage defining an inner surface;
the adhesive is disposed within the ferrule and in contact with the inner surface of the ferrule and the optical fiber; and
the adhesive comprises a cured alkyltrialkoxysilane, a cured aryltrialkoxysilane, and a cured aryltrifluoro silane.
18. The optical connector of claim 17 , wherein the adhesive further comprises cured tetraethyl orthosilicate or the optical connector comprises a cured tetraethyl orthosilicate layer disposed between the optical fiber and the adhesive.
19. The optical connector of claim 17 , wherein the adhesive comprises a cured sol mixture.
20. An optical connector for terminating an optical fiber, the optical connector comprising a fiber receiving passage, the optical fiber, and an adhesive, wherein:
the fiber-receiving passage defines an inner surface;
the adhesive is disposed within the fiber receiving passage and in contact with the inner surface of the fiber receiving passage and the optical fiber; and
the adhesive comprises a cured alkyltrialkoxysilane, a cured aryltrialkoxysilane, and a cured aryltrifluoro silane.