Superabsorbent polymer having a capacity increase

1. A superabsorbent polymer comprising a polymerized monomer selected from an ethylenically unsaturated carboxylic acid, ethylenically unsaturated carboxylic acid anhydride, salts or derivatives thereof, and an internal crosslinker agent comprising an internal crosslinking agent wherein the internal crosslinker agent comprises a silane compound comprising at least one vinyl group or allyl group and at least one Si—O bond wherein the vinyl group or allyl group is directly attached to a silicon atom, wherein the superabsorbent polymer composition is a particulate superabsorbent composition.

2. The particulate superabsorbent polymer of claim 1 , wherein the particulate superabsorbent polymer has a Centrifuge Retention Capacity of from about 25 g/g to about 55 g/g as set forth herein in the Centrifuge Retention Capacity Test.

3. The particulate superabsorbent polymer of claim 1 , wherein the particulate superabsorbent polymer has a Absorbency Under Load at 0.9 psi of about 15 g/g to about 25 g/g as set forth herein in the Absorbency Under Load at 0.9 psi Test.

4. The particulate superabsorbent polymer of claim 1 having a Gel Bed Permeability of from about 10×10 −8 cm 2 to about 300×10 −8 cm 2 as set forth herein in the Gel Bed Permeability Test.

5. The particulate superabsorbent polymer of claim 1 , wherein said silane compound is selected from one of the following

wherein

R 1 represents C 2 to C 3 alkenyl,

R 2 represents H, C 1 to C 4 alkyl, C 2 to C 5 alkenyl, C 6 to C 8 aryl, C 2 to C 5 carbonyl,

R 3 represents H, C 1 to C 4 alkyl, C 6 to C 8 aryl,

R 4 and R 5 independently represent H, C 1 to C 4 alkyl, C 6 to C 8 aryl,

m represents an integer of from 1 to 2,

n represents an integer of from 2 to 3,

l represents an integer of from 0 to 1,

m+n+l= 4,

x represents an integer larger than 1, and

y represents an integer of 0 or larger than 0.

6. The particulate superabsorbent polymer according to claim 5 wherein said silane compound is selected from vinyltriisopropenoxy silane, vinyltriacetoxysilane, vinyltrimethoxysilane, vinyltriethoxysilane, diethoxymethylvinyl silane, and polysiloxane comprising at least two vinyl groups.

7. The particulate superabsorbent polymer of claim 1 further comprising a second internal crosslinker agent.

8. The particulate superabsorbent polymer of claim 7 wherein the second internal crosslinker is selected from polyethylene glycol monoallyl ether acrylate, ethoxylated trimethylol propane triacrylate, or polyethylene glycol diacrylate.

9. The particulate superabsorbent polymer of claim 1 wherein the polymerized monomer has a neutralization of at least 50 mol %.

10. A particulate superabsorbent polymer composition comprising a superabsorbent polymer comprising:

a) at least one monomer selected from an ethylenically unsaturated carboxylic acid, ethylenically unsaturated carboxylic acid anhydride, salts or derivatives thereof based on the superabsorbent polymer;

b) from about 0.001% by weight to about 5% by weight of a first internal crosslinking agent and second internal crosslinking agent, based on the monomer of a) wherein the first internal crosslinking agent comprises a silane compound comprising at least one vinyl group or allyl group and at least one Si—O bond wherein the vinyl group or allyl group is directly attached to a silicon atom; and

c) a salt forming cation wherein the superabsorbent polymer has a degree of neutralization of greater than about 25%;

wherein elements a), b) and c) are polymerized into a crosslinked hydrogel, which is then prepared into superabsorbent polymer particles; and the particulate superabsorbent polymer composition further comprises a surface coating comprising ethylene carbonate, aluminum sulfate and maleated polypropylene, wherein said particulate superabsorbent polymer composition has a Centrifuge Retention Capacity of from 25 g/g to about 55 g/g as set forth herein in the Centrifuge Retention Capacity Test.

11. The particulate superabsorbent polymer composition of claim 10 wherein said silane compound is selected from one of the following

wherein

R 1 represents C 2 to C 3 alkenyl,

R 2 represents H, C 1 to C 4 alkyl, C 2 to C 5 alkenyl, C 6 to C 8 aryl, C 2 to C 5 carbonyl,

R 3 represents H, C 1 to C 4 alkyl, C 6 to C 8 aryl,

R 4 and R 5 independently represent H, C 1 to C 4 alkyl, C 6 to C 8 aryl,

m represents an integer of from 1 to 2,

n represents an integer of from 2 to 3,

l represents an integer of from 0 to 1,

m+n+l= 4,

x represents an integer larger than 1, and

y represents an integer of 0 or larger than 0.

12. The particulate superabsorbent polymer composition according to claim 11 wherein said silane compound is selected from vinyltriisopropenoxy silane, vinyltriacetoxysilane, vinyltrimethoxysilane, vinyltriethoxysilane, diethoxymethylvinyl silane, and polysiloxane comprising at least two vinyl groups.

13. The particulate superabsorbent polymer composition of claim 10 having a Gel Bed Permeability of from about 50×10 −8 cm 2 to about 300×10 −8 cm 2 as set forth herein in the Gel Bed Permeability Test.

14. The particulate superabsorbent polymer composition of claim 10 further comprising a second internal crosslinker.

15. The particulate superabsorbent polymer composition of claim 14 wherein the second internal crosslinker is selected from polyethylene glycol monoallyl ether acrylate, ethoxylated trimethylol propane triacrylate, or polyethylene glycol diacrylate.