Ni-based alloy for welding material and welding wire, rod and power
View Patent ↗A Ni-based alloy for a welding material including, by mass, 0.001 to 0.1% of C, 18 to 25% of Co, 16 to 20% of Cr, 2.5 to 3.5% of Al, 9.0 to 15.0% of Mo+W, 0.001 to 0.03% of B and the balance being Ni and inevitable impurities.
1. A product having a welded portion formed of a Ni-based alloy for a welding material used at a temperature of 700 to 800° C. comprising, by mass, 0.01 to 0.04% of C, 18 to 25% of Co, 16 to 20% of Cr, 2.5 to 3.5% of Al, more than 11.5% and up to 14.0% or less of Mo+W, 0.001 to 0.03% of B and the balance being Ni and inevitable impurities,
wherein the welded portion has a y′ (Ni 3 Al) strengthening phase, a solid solution temperature of the y′ (Ni 3 Al) strengthening phase being in a range of 850 to 900° C., and a precipitation amount of the y′ (Ni 3 Al) strengthening phase at 800° C. being 10 to 25% by volume.
2. The product according to claim 1 , wherein the Ni-based alloy contains, by mass, 20 to 23% of Co, 17 to 19% of Cr, 2.8 to 3.2% of Al, 10.0 to 12.0% of Mo+W and 0.003 to 0.01% of B.
3. The product according to claim 1 , wherein a creep rupture time of the welded portion under conditions of 800° C. and 294 MPa is 200 hours or longer.
4. A welding wire for forming the welded portion of the product according to claim 1 .
5. A welding rod for forming the welded portion of the product according to claim 1 .
6. A welding powder for forming the welded portion of the product according to claim 1 .