CARBON-FIBER-REINFORCED SILICON-CARBIDE-BASED COMPOSITE MATERIAL AND BRAKING MATERIAL
A carbon-fiber-reinforced silicon-carbide-based composite material which has better strength and toughness, and a braking material, such as a brake disc using the composite material, are provided. By using the carbon-fiber-reinforced silicon-carbide-based composite material including a bundle of fibers having chopped carbon fibers arranged in parallel and the other carbon component, carbon, silicon, and silicon carbide, in which the fiber bundle is flat, its cross-section perpendicular to its longitudinal direction has a larger diameter of 1 mm or more, a ratio of the larger diameter to a smaller diameter is from 1.5 to 5, and a plurality of the fiber bundles are randomly oriented substantially along a two-dimensional plane, and a two-dimensional side serves as a braking side to thereby constitute the braking material.
1 . A carbon-fiber-reinforced silicon-carbide-based composite material, comprising a bundle of fibers having chopped carbon fibers arranged in parallel and the other carbon component, carbon, silicon, and silicon carbide, wherein
said fiber bundle is flat, its cross-section perpendicular to its longitudinal direction has a larger diameter of 1 mm or more, a ratio of the larger diameter to a smaller diameter is from 1.5 to 5, and a plurality of said fiber bundles are randomly oriented substantially along a two-dimensional plane.
2 . A carbon-fiber-reinforced silicon-carbide-based composite material as claimed in claim 1 , wherein said chopped carbon fiber has a diameter of from 7 μm to 15 μm and a length of from 4 mm to 14 mm, and a distance between adjacent chopped carbon fibers is from 1 μm to 20 μm at the cross-section perpendicular to the longitudinal direction of said fiber bundle.
3 . A carbon-fiber-reinforced silicon-carbide-based composite material as claimed in claim 1 , wherein in an arbitrary section perpendicular to said two-dimensional plane, a ratio of an area occupied by said chopped carbon fibers to the section is from 30% to 45%, a ratio of an area occupied by silicon carbide to the section is from 40% to 59%, and the remainder is of silicon and carbon components other than said chopped carbon fibers.
4 . A carbon-fiber-reinforced silicon-carbide-based composite material as claimed in claim 1 , wherein said fiber bundle includes a first fiber bundle having a length of from 4 mm to 8 mm and a second fiber bundle having a length of from 10 mm to 14 mm, and an area ratio between said first fiber bundle and said second fiber bundle is within a range of from 9:1 to 7:3 at an arbitrary section along said two-dimensional plane.
5 . A carbon-fiber-reinforced silicon-carbide-based composite material as claimed in claim 1 , wherein in a surface layer between at least 500 μm and maximum 4000 μm in depth from the surface, a total content of said silicon carbide and the silicon carbide resulting from silicifying the chopped carbon fibers and the other carbon component is from 50% by weight to 80% by weight.
6 . A braking material using the carbon-fiber-reinforced silicon-carbide-based composite material as claimed in claim 5 , wherein at least one of two-dimensional sides of said surface layer serves as a braking side.