Aluminum alloys and methods for producing the same
View Patent ↗Heat treatable aluminum alloy strips and methods for making the same are disclosed. The heat treatable aluminum alloy strips are continuously cast and quenched, with optional rolling occurring before and/or after quenching. After quenching, the heat treatable aluminum alloy strip is neither annealed nor solution heat treated.
1. A method comprising:
(a) continuously casting a 6xxx heat treatable aluminum alloy strip via a casting apparatus;
(i) wherein the continuously casting comprises casting at a speed of 25 to 400 feet per minute and using roll separating forces of from 25 to 300 pounds per inch of width cast;
(ii) wherein the 6xxx heat treatable aluminum alloy strip exits the casting apparatus at a temperature below its solidus temperature;
(iii) wherein the 6xxx heat treatable aluminum alloy strip has a gauge of from 0.040 inch to 0.249 inch;
(b) after the continuously casting step, hot rolling and quenching the 6xxx heat treatable aluminum alloy strip via a hot rolling apparatus;
(i) wherein the quenching occurs (A) during the hot rolling, or (B) both during and after the hot rolling;
(ii) wherein the 6xxx heat treatable aluminum alloy strip exits the hot rolling apparatus at a temperature of from 550° F. to 900° F.; and
(c) after the hot rolling and quenching step (b), artificially aging the 6xxx heat treatable aluminum alloy strip;
wherein, after the hot rolling and quenching step (b), the method excludes both (i) annealing of the 6xxx heat treatable aluminum alloy strip, and (ii) solution heat treating of the 6xxx heat treatable aluminum alloy strip.
2. The method of claim 1 , comprising:
after the hot rolling and quenching step (b) and prior to the artificially aging step (c), cold rolling the 6xxx heat treatable aluminum alloy strip.
3. The method of claim 1 , wherein the continuously casting step (a) comprises:
(A) delivering a molten aluminum alloy to a pair of spaced apart rotating casting rolls defining a nip therebetween;
(B) advancing the molten aluminum alloy between surfaces of the casting rolls, wherein a freeze front of metal is formed at the nip; and
(C) withdrawing the 6xxx heat treatable aluminum alloy strip from the nip.
4. The method of claim 1 , wherein the method consists of steps (a), (b), and (c).
5. The method of claim 1 , wherein the artificial aging comprises aging to a T5 temper.
6. The method of claim 1 , wherein, the hot rolling is hot rolling to a final gauge.