NdFeB sintered magnet and method for producing the same
A method for producing an NdFeB sintered includes forming a layer containing Dy and/or Tb on the surface of an NdFeB sintered magnet base material and then performing a grain boundary diffusion process for diffusing Dy and/or Tb from the aforementioned layer through the crystal grain boundaries of the magnet base material into the magnet base material by heating the magnet base material to a temperature equal to or lower than the sintering temperature thereof. In this method: a) the content of a rare earth in a metallic state in the magnet base material is equal to or higher than 12.7 at %; b) the aforementioned layer is a powder layer formed by depositing a powder; and c) the powder layer contains Dy and/or Tb in a metallic state by an amount equal to or higher than 50 mass %.
1. An NdFeB sintered magnet with Dy and/or Tb diffused through grain boundaries by a grain boundary diffusion method, wherein:
a magnet base material is a plate-shaped magnet base material having a thickness of 3.5 mm or greater;
the magnet base material does not contain Tb;
an amount of a rare earth in a metallic state contained in the plate-shaped magnet base material is 12.7 at % or greater;
a total amount of O, C and N contained in the plate-shaped magnet base material is 2900 ppm or less;
in a grain of the NdFeB sintered magnet, more Dy and/or Tb exist on a surface of the grain than inside of the grain;
in the NdFeB sintered magnet, more Dy and/or Tb exist on a surface of the NdFeB sintered magnet than inside of the NdFeB sintered magnet;
the NdFeB sintered magnet has a coercivity between 1.6 MA/m and 1.96 MA/m;
the NdFeB sintered magnet has a residual flux density between 1.27 T and 1.38 T; and
the NdFeB sintered magnet has a squareness value between 90% and 94%.
2. The NdFeB sintered magnet according to claim 1 , wherein Al is contained on the surface of the grain of the NdFeB sintered magnet on a surface of the NdFeB sintered magnet.
3. The NdFeB sintered magnet according to claim 1 , wherein Co and/or Ni is contained on the surface of the grain of the NdFeB sintered magnet and on a surface of the NdFeB sintered magnet.