Method for manufacturing a precipitation-hardening cold-rolled steel sheet having excellent yield ratios
A method for manufacturing a precipitation hardening cold-rolled steel sheet with an excellent yield ratio. The method may include the steps of hot rolling a steel slab with finish rolling at a temperature of Ar3 transformation point or more to form a hot-rolled steel sheet, coiling the hot-rolled steel sheet at a temperature of 550-600 ° C., cold rolling the hot-rolled steel sheet at a reduction ratio of 50% or more; and recovery-recrystallization annealing the cold-rolled steel sheet at a line speed of 150-200 mpm and at a temperature of 780-820° C. in a continuous annealing furnace. The recovery-recrystallization annealing may provide a recrystallization ratio of 65-75%. The steel slab includes, by weight %: C: 0.07-0.10%, Mn: 1.41-1.70%, P: 0.05-0.07%, S: 0.005% or less, N: 0.005% or less, acid-soluble Al: 0.10-0.15%, Nb: 0.06-0.09%, B: 0.0008-0.0012%, Sb: 0.02-0.06%, and the balance comprising Fe and other unavoidable impurities.
1. A method for manufacturing a precipitation-hardening cold-rolled steel sheet, comprising:
hot rolling a steel slab with finish rolling at a temperature of Ar3 transformation point or more to form a hot-rolled steel sheet, the steel slab comprising, by weight %: C: 0.07-0.10%, Mn: 1.41-1.70%, P: 0.05-0.07%, S: 0.005% or less, N: 0.005% or less, acid-soluble Al: 0.10-0.15%, Nb: 0.06-0.09%, B: 0.0008-0.0012%, Sb: 0.02-0.06%, and the balance comprising Fe and other unavoidable impurities;
cold rolling the hot-rolled steel sheet at a reduction ratio of 50% or more; and
recovery-recrystallization annealing the cold-rolled steel sheet at a line speed of 150-200 mpm and at a temperature of 780-820° C. in a continuous annealing furnace,
wherein a yield ratio of the cold-rolled steel sheet is 85% or more.
2. The method according to claim 1 , further comprising:
coiling the hot-rolled steel sheet at a temperature of 550-600° C.
3. The method according to claim 1 , wherein the recovery-recrystallization annealing is performed at a recrystallization ratio of 65-75%.
4. The method according to claim 1 , wherein the cold-rolled steel sheet comprises acicular ferrite structure.
5. The method according to claim 4 , wherein:
the acicular ferrite structure is formed by NbC precipitates reacting with the B, and
the NbC precipitates are formed by adding the Nb and the B in combination.