A method for manufacturing a hot-rolled sheet attains grain refinement of the steel sheet whose grain size is extremely fine. In particular, a ferrite grain size of less than average 2 μm is obtained, which is not laminar but has ferrite grains with equiaxed morphology and exhibits high formability in forming. The method comprises the steps of rolling and cooling, wherein the rolling reductions, cooling steps, and temperature are closely regulated. A hot rolled sheet made from the method of manufacturing has a controlled ferrite grain in different regions of sheet thickness.
1. A hot-rolled sheet containing 0.04-0.20% C, 0.01-2.0% Si, 0.5-3.0% Mn by mass, and the reminder being Fe and inevitable impurities,
a size D2 of ferrite grain at a quarter region of sheet thickness from the surfaces of the hot-rolled sheet being less than 2.0 μm,
the relation among the size D2 of ferrite grain, a size D3 of ferrite grain at a central region of sheet thickness from the surfaces of the hot-rolled sheet, and a size D1 of ferrite grain at a position 50 μm in depth of sheet thickness from the surfaces of the hot-rolled sheet satisfying the expression:
( D 3− D 1)/ D 2≦0.4, and
a grain size Dr in the rolling direction and a grain size Dt in the thickness direction of the ferrite grain at a position 50 μm in depth of sheet thickness from the surfaces of the hot-rolled sheet satisfying the expression (1)
|( Dr−Dt )/(( Dr+Dt )/2)|≦0.25 (1).