Sintered alloy and production method therefor
View Patent ↗A sintered alloy has an overall composition consisting of, by mass %, 13.05 to 29.62% of Cr, 6.09 to 23.70% of Ni, 0.44 to 2.96% of Si, 0.2 to 1.0% of P, 0.6 to 3.0% of C, and the balance of Fe and inevitable impurities; a metallic structure in which carbides are precipitated and uniformly dispersed in an iron alloy matrix having dispersed pores; and a density of 6.8 to 7.4 Mg/m 3 . The carbides include specific carbides having maximum diameter of 1 to 10 μm and area ratio of 90% or more with respect to the total carbides.
1. A sintered alloy comprising:
an overall composition consisting of, by mass %, 13.05 to 29.62% of Cr, 6.09 to 23.70% of Ni, 0.44 to 2.96% of Si, 0.2 to 1.0% of P, 0.6 to 3.0% of C, and the balance of Fe and inevitable impurities;
an austenitic structure in which carbides are precipitated and uniformly dispersed in an iron alloy matrix having dispersed pores; and
a density of 6.8 to 7.4 Mg/m 3 ,
wherein the carbides include carbides having a maximum diameter of 1 to 10 μm, which have an area ratio of 90% or more with respect to that of the total carbides.
2. The sintered alloy according to claim 1 , wherein nitrides are formed on a surface of the sintered alloy and inner surfaces of the pores.
3. A production method for sintered alloy, the method comprising:
preparing an Fe alloy powder, an Fe—P alloy powder, and a graphite powder,
the Fe alloy powder consisting of, by mass %, 15 to 30% of Cr, 7 to 24% of Ni, 0.5 to 3.0% of Si, optionally 3.0% or less of at least one of Mo, V, W, Nb, and Ti, and the balance of Fe and inevitable impurities, the Fe—P alloy powder consisting of 10 to 30 mass % of P and the balance of Fe and inevitable impurities;
mixing the Fe—P powder and 0.6 to 3.0 mass % of the graphite powder with the Fe alloy powder into a mixed powder, such that the amount of P is 0.2 to 1.0 mass % with respect to the overall composition of the mixed powder;
compacting the mixed powder into a green compact having a density of 6.0 to 6.8 Mg/m 3 , and
sintering the green compact at a temperature of 1100 to 1160° C. in a non-oxidizing gas at normal pressure.
4. The production method for sintered alloy according to claim 3 , wherein the non-oxidizing gas is nitrogen gas or a mixed gas of nitrogen and hydrogen that contains at least 10 volume % nitrogen.
5. A sintered alloy produced by the production method recited in claim 3 comprising:
an overall composition consisting of, by mass %, 13.05 to 29.62% of Cr, 6.09 to 23.70% of Ni, 0.44 to 2.96% of Si, 0.2 to 1.0% of P, 0.6 to 3.0% of C, 2.96% or less of at least one of Mo, V, W, Nb, and Ti, and the balance of Fe and inevitable impurities;
an austenitic structure in which carbides are precipitated and uniformly dispersed in an iron alloy matrix having dispersed pores; and
a density of 6.8 to 7.4 Mg/m 3 ,
wherein the carbides include carbides having maximum diameter of 1 to 10 μm, which have an area ratio of 90% or more with respect to that of the total carbides.
6. The sintered alloy according to claim 5 , wherein nitrides are formed on a surface of the sintered alloy and inner surfaces of the pores.