ELECTRICALLY CONDUCTIVE POLYPHENYLENE SULFIDE COMPOUNDS
An electrically conductive polymer compound is disclosed. The compound comprises a matrix comprising polyphenylene sulfide and carbon nanotubes and glass fibers dispersed in the matrix. The carbon nanotubes are disaggregated and disagglomerated within the polyphenylene sulfide, when the compound is viewed at 20,000× magnification. The compound is useful for making extruded or molded plastic articles that need electrical properties.
1 . An electrically conductive thermoplastic compound, comprising
(a) polyphenylene sulfide;
(b) glass fibers; and
(c) carbon nanotubes dispersed in an amount ranging from about 0.1 to about 10 weight percent of the compound in the polyphenylene sulfide, without aggregation or agglomeration of nanotubes in the polyphenylene sulfide when the compound is viewed at 20,000× magnification, wherein the compound has a specific gravity of at least about 1.5.
2 . The compound of claim 1 , wherein the carbon nanotubes are single-wall nanotubes.
3 . The compound of claim 1 , wherein the carbon nanotubes are multi-wall nanotubes.
4 . The compound of claim 1 , further comprising an optional second polymer selected from the group consisting of liquid crystal polymer, polystyrene, polyimide, polyarylsufone, polyphenylene oxide (polyphenylene ether), polyarylcarbonates, polyamide, fluoropolymer, and combinations thereof.
5 . The compound of claim 1 , further comprising an optional functional additive selected from the group consisting of adhesion promoters; biocides (antibacterials, fungicides, and mildewcides), anti-fogging agents; anti-static agents; bonding agents; dispersants; fillers and extenders; fire and flame retardants and smoke suppresants; impact modifiers; initiators; lubricants; micas; pigments, colorants and dyes; plasticizers; processing aids; release agents; silanes, titanates and zirconates; slip and anti-blocking agents; stabilizers; stearates; ultraviolet light absorbers; viscosity regulators; waxes; catalyst deactivators, and combinations of them.
6 . The compound of claim 1 , wherein the carbon nanotubes have an aspect ratio ranging from 10:1 to 10,000:1.
7 . The compound of claim 1 , wherein the carbon nanotubes have a diameter ranging from about 0.5 nm to about 1000 nm.
8 . The compound of claim 1 , wherein the amount of polyphenylene sulfide polymer ranges from about 5 to about 94 weight percent of the compound and wherein the carbon nanotubes range from about 0.1 to about 10 weight percent of the compound.
9 . A molded plastic article made from the compound of claim 1 .
10 . A method of making a compound of claim 1 , comprising the steps of
(a) melting polyphenylene sulfide in multiple zones of a twin screw extruder;
(b) at another zone downstream of the multiple zones, mixing into the melted polyphenylene sulfide both glass fibers and carbon nanotubes.