HEAT RESISTANT, FLAME RETARDANT POLYLACTIC ACID COMPOUNDS
Significant disadvantages of the use of polylactic acid (PLA), lack of good heat stability and flame retardance, have been overcome by the use of an aryl phosphate in combination with talc. The compound achieves a threshold of 65° C. in heat deflection temperature and V-0 flame retardance at 1.6 mm thickness.
1 . A heat resistant, flame retardant, polylactic acid compound, comprising:
(a) polylactic acid;
(b) polycarbonate;
(c) talc in an amount from about 1 to about 8 weight percent of the compound; and
(d) aryl phosphate,
wherein the compound has a moisture content of less than 0.2%;
wherein the aryl phosphate is selected from the group consisting of
(i) resorcinol bis (diphenyl phosphate) and
(ii) an oligomeric, free flowing solid aryl phosphate ester flame retardant, having a phosphorus content of 10.7%, a specific gravity of 1.3, a melting range of 101-108° C., and a triphenyl phosphate content of less than about 1 percent; and
wherein the compound has a V-0 rating when tested according to ASTM Test No. D-635 at 1.6 mm thickness.
2 . (canceled)
3 . (canceled)
4 . The compound of claim 1 , wherein the aryl phosphate is resorcinol bis (diphenyl phosphate), wherein the compound has talc in an amount from about 2 to about 4 weight percent of the compound, and wherein the compound has a V-0 rating when tested according to ASTM Test No. D-635 at 0.8 mm thickness.
5 . The compound of claim 1 , wherein the compound has a heat distortion temperature of greater than 65 degrees C. when tested according to ASTM D-648 at 66 PSI.
6 . The compound of claim 1 , wherein the compound has talc in an amount less than about 8 weight percent of the compound, wherein the compound has resorcinol bis (diphenyl phosphate) as the aryl phosphate in an amount less than about 15 weight percent of the compound, and wherein the compound has a heat distortion temperature of greater than 69 degrees C. when tested according to ASTM D-648 at 66 PSI.
7 . The compound of claim 1 , wherein acrylic impact modifier is present optionally in an amount of from about 1 to about 15 weight percent of the compound.
8 . The compound of claim 1 , wherein the polylactic acid comprises poly-D-lactide, poly-L-lactide, or a combination of both and wherein the amount of polylactic acid is present in the compound ranges from about 20 to about 50 weight percent.
9 . The compound of claim 1 , wherein the polycarbonate is present in the compound from about 40 to about 60 weight percent.
10 . The compound of claim 7 , wherein the impact modifier is a core/shell acrylic polymer or a silicone-acrylic-based rubber.
11 . The compound of claim 1 , further comprising optional additives selected from the group consisting of adhesion promoters; biocides; anti-fogging agents; anti-static agents; bonding, blowing and foaming agents; dispersants; initiators; lubricants; pigments, colorants and dyes; plasticizers; processing aids; release agents; slip and anti-blocking agents; stabilizers; stearates; ultraviolet light absorbers; viscosity regulators; waxes; and combinations of them
12 . A plastic article shaped from a compound of claim 1 .
13 . The article of claim 12 , wherein the article is molded or extruded and wherein the article is shaped for use in transportation, appliance, electronics, building and construction, packaging, or consumer markets.
14 . A method of making the compound of claim 1 , comprising the steps of
(a) gathering ingredients including polylactic acid, polycarbonate, talc, and aryl phosphate,
(b) melt-mixing them into a compound for subsequent shaping into a plastic article shaped for use in transportation, appliance, electronics, building and construction, packaging, or consumer markets.
15 . The method of making the compound of claim 14 , further comprising the steps of
(c) drying the compound to a moisture content of less than 0.2% and
(d) shaping the compound into a plastic article for use in transportation, appliance, electronics, building and construction, packaging, or consumer markets.
16 . The compound of claim 1 , wherein the polylactic acid comprises poly-D-lactide, poly-L-lactide, or a combination of both and wherein the amount of polylactic acid present in the compound is at least about 30 weight percent of the compound.