1. A composition for a thermal insulation material, comprising:

a magnesium oxychloride cement MOC comprising magnesium oxide, magnesium chloride, and water, wherein the magnesium oxychloride cement comprises a molar ratio of the magnesium oxide to the magnesium chloride of 9 to 17, and a weight ratio of the water to the magnesium oxide and the magnesium chloride of 0.3 to 0.9 for forming a plurality of MOC fibrous product layers having a first refractive index of 1.60 to 1.80;

a plurality of air-filled beads, wherein each of the air-filled beads comprises a shell thickness in a range of 10 nm to 10 μm, a density of 0.1 to 2.6 g/cm 3 , and a second refractive index of 1.40 to 2.50; and

0.1-10 volume % titanium dioxide (TiO 2 ), 0.1-50 volume % fly ash, 0.1-20 volume % pigment, 0.1-5 volume % potassium dihydrogen phosphate (KH 2 PO 4 ) and 0.1-5 volume % sodium dihydrogen phosphate (NaH 2 PO 4 );

wherein the air-filled beads constitute a volume fraction of the thermal insulation material for forming the MOC fibrous product layers with a network layer thickness in a range of 10 nm to 5 μm; and

wherein the MOC fibrous product layers having the first refractive index in the range of 1.60 to 1.80 and the network layer thickness in the range of 10 nm to 5 μm are adjacent to the air-filled beads having the shell thickness in the range of 10 nm to 10 μm and the second refractive index of 1.40 to 2.50, providing that the thermal insulation material comprises a multi-layered structure for reflecting incident electromagnetic wave.

2. The composition of claim 1 , wherein said thermal insulation material reflects the incident electromagnetic wave, k, according to the equation:

n

i

⁢

d

i

+

n

j

⁢

d

j

=

λ

k

4

⁢

⁢

to

⁢

⁢

λ

k

2

,

where d i denotes the network layer thickness, n i denotes the first refractive index, d j denotes the shell thickness, n j denotes the second refractive index, and λ k is a wavelength of said wave.

3. The composition of claim 1 , wherein said wave is selected from visible, near infrared, middle infrared, far infrared and other heat waves.

4. The composition of claim 1 , wherein said pigment is iron dioxide or reflective ones.

5. The composition of claim 1 , wherein the first refractive index of the MOC fibrous product layer is 1.70.

6. The composition of claim 1 , wherein said air-filled beads constitute 80% volume fraction of the thermal insulation material and comprise air-filled beads made of glass.

7. The composition of claim 1 , wherein the second refractive index of the air-filled beads has a value of 1.51.

8. The composition of claim 1 , wherein the shell thickness of the air-filled beads has a value of 431 nm.

9. The composition of claim 1 , wherein said composition is applied onto an object or a structure including a railway track, a shelter for animals or human, or a pipeline for transporting a gas or liquid.

10. The composition of claim 1 , wherein the shell thickness has a value of 431 nm, and the second refractive index has a value of 1.51, the composition further comprises 15.29 vol % of the magnesium oxide, 4.75 vol % of the magnesium chloride, and 0.11 vol % of potassium dihydrogen phosphate.

11. A composition for a thermal insulation material, comprising: 14.96-19.84 vol % of magnesium oxide, 4.65-6.16 vol % of magnesium chloride, 20.33-30.04 vol % of air-filled glass beads, titanium dioxide, 0.11-0.14 vol % of potassium dihydrogen phosphate, and 49.81-52.59 vol % of water, wherein the air-filled glass beads comprise a refractive index of 1.51 and a wall thickness of 431 nm, providing that the thermal insulation material comprises a multi-layered structure for reflecting incident electromagnetic wave.

12. A composition for a thermal insulation material, comprising:

a magnesium oxychloride cement MOC comprising magnesium oxide, magnesium chloride, and water, wherein the magnesium oxychloride cement comprises a molar ratio of the magnesium oxide to the magnesium chloride of 9 to 17, and a weight ratio of the water to the magnesium oxide and the magnesium chloride of 0.3 to 0.9 for forming a plurality of MOC fibrous product layers having a first refractive index of 1.60 to 1.80;

a plurality of air-filled beads, wherein each of the air-filled beads comprises a shell thickness having a value of 431 nm, a density of 0.1 to 2.6 g/cm 3 , and a second refractive index of 1.51; and

15.29 vol % of the magnesium oxide, 4.75 vol % of the magnesium chloride, and 0.11 vol % of potassium dihydrogen phosphate;

wherein the air-filled beads constitute a volume fraction of the thermal insulation material for forming the MOC fibrous product layers with a network layer thickness in a range of 10 nm to 5 μm; and

wherein the MOC fibrous product layers having the first refractive index in the range of 1.60 to 1.80 and the network layer thickness in the range of 10 nm to 5 μm are adjacent to the air-filled beads having the shell thickness in the range of 10 nm to 10 μm and the second refractive index of 1.40 to 2.50, providing that the thermal insulation material comprises a multi-layered structure for reflecting incident electromagnetic wave.

13. The composition of claim 12 , wherein said air-filled beads constitute 80% volume fraction of the thermal insulation material and comprise air-filled beads made of glass.