Multilayer hydrogels with pH-responsive swelling and surface wettability
A novel type of ultrathin cationic hydrogel coatings are provided that have high, quick and reversible swelling/shrinkage transitions and surface wettability in response to pH changes. The poly(4-vinyl pyridine) (PVP) hydrogel films are produced by selective cross-linking of PVP copolymers in layer-by-layer (LbL) films assembled by spin-assisted method. These multilayer hydrogels exhibit drastic and reversible 10-fold swelling when the pH is changed from neutral to acidic. The swelling amplitude of these coatings is controlled by varying cross-link densities within the films. The pH-responsive hydrogels open new prospects for developing “intelligent” materials with sharp stimuli-triggered responses for applications in sensing, transport regulation, and self-cleaning coatings.
1. A pH-responsive layered composition comprising at least two spin-assisted layer-by-layer spun copolymer layers, wherein the spun layers have a plurality of cross-linkable side-groups attached thereto, and wherein the spun layered composition when hydrated swells when protonated and has a reduced volume when deprotonated, wherein the at least two spun copolymer layers are comprised of a polyvinylpyridine copolymer and are cross-linked.
2. The pH-responsive layered composition of claim 1 , wherein the at least two copolymer spun layers consist essentially of copolymers (PVP-NH 2 -m) of poly(4-vinylpyridine-NH 2 -1), poly(4-vinylpyridine-NH 2 -4), or poly(4-vinylpyridine-NH 2 -7).
3. The pH-responsive layered composition of claim 1 , wherein the at least two copolymer spun layers are separated by alternating spun copolymer layers comprising a copolymer comprising poly(methacrylic acid).
4. The pH-responsive layered composition of claim 1 , wherein the cross-linkable side-groups are carboxylate groups, cationic amino groups, or a combination thereof.
5. The pH-responsive layered composition of claim 4 , wherein the cross-linkable side-groups are cationic amino groups.
6. The pH-responsive layered composition of claim 1 , wherein the copolymer spun layers are cross-linked with glutaraldehyde.
7. The pH-responsive layered composition of claim 1 , comprising from 2 to about 50 spun layers, wherein each of the spun layers comprises a poly(vinylpyridine-NH 2 ) copolymer or alternates with a spun layer comprising a poly(methacrylic acid) copolymer.
8. A pH-responsive spin-assisted layer-by-layer layered composition comprising at least two glutaraldehyde cross-linked spun layers of a copolymer comprising 4-vinylpyridine and having a plurality of amino side-groups attached thereto, and wherein the spun layered composition when hydrated swells when protonated and has a reduced volume when deprotonated.
9. The pH-responsive layered composition according to claim 8 , comprising spun layers of a copolymer consisting essentially of 4-vinylpyridine, and wherein the layered composition is substantially dehydrated.
10. A method of forming a pH-responsive composition, the method comprising the steps of:
(a) generating a polyvinylpyridine copolymer having a plurality of cross-linkable side-groups attached thereto;
(b) generating a layer-by-layer composition by spin-assisted deposition of the polyvinylpyridine copolymer on a support material; and
(c) cross-linking the spun layers of the layer-by-layer composition, thereby generating a pH-responsive spin-assisted layer-by-layer layered composition comprising at least two cross-linked spun polyvinylpyridine copolymer layers, wherein the spun-layered composition when hydrated reversible swells when protonated.
11. The method according to claim 10 , further comprising the steps of:
generating a poly(methacrylic acid) copolymer;
spin-assisted deposing the poly(methacrylic acid) copolymer on each of the polyvinylpyridine copolymer layers;
cross-linking the polyvinylpyridine copolymer layers; and
removing poly(methacrylic acid) copolymer layers under acid conditions.
12. The method according to claim 10 , wherein the support material is a silicon surface, and wherein the support material is coated with an agent enhancing the attachment of a copolymer layer to the silicon surface.
13. The method according to claim 12 , wherein the agent coating the silicon surface is poly(glycidylmethacrylate).
14. The method according to claim 10 , wherein the pH-responsive spin-assisted layer-by-layer layered composition consists essentially of cross-linked layers of a poly(vinylpyridine-NH 2 ).
15. The method according to claim 10 , further comprising the step of drying the spin-assisted layer-by-layer layered composition.
16. The method according to claim 10 , further comprising the step of displacing the composition from the support material.