Injection molding of poly-4-hydroxybutyrate
View Patent ↗Compositions of P4HB and processes to injection mold these compositions have been developed. These compositions are prepared from P4HB polymers and blends having intrinsic viscosities less than 3.2 dl/g but greater than 0.8 dl/g, moisture contents of less than 0.5% by weight, and more preferably less than 0.05% by weight, and using a polymer melt temperature during molding of at least 150° C. A preferred embodiment comprises a P4HB molding with an intrinsic viscosity of less than 3.2 dl/g that degrades rapidly in vivo.
1. A process for producing moldings comprising poly-4-hydroxybutyrate the process comprising
feeding a poly-4-hydroxybutyrate (P4HB) polymer with an intrinsic viscosity between 0.8 and 3.2 dl/g, and a moisture content of less than 0.5% by weight, to an injection molding machine,
melting the polymer at a temperature of at least 150° C.,
injecting the melted polymer into a mold set at a temperature less than the melt temperature of the polymer under pressure effective to fill the mold, and
holding the polymer in the mold for a time period effective to form a molding.
2. The process of claim 1 wherein the intrinsic viscosity of the P4HB polymer decreases less than 25% upon molding.
3. The process of claim 1 wherein the intrinsic viscosity of the P4HB polymer decreases less than 10% upon molding.
4. The process of claim 1 wherein the molding is subsequently annealed at a temperature of less than 60° C.
5. The process of claim 4 wherein the melt temperature of the molding increases more than 1° C. upon annealing at 45° C.
6. The process of claim 4 wherein the melt temperature of the molding increases more than 4° C. upon annealing at 50° C.
7. The process of claim 4 wherein the melt temperature of the molding increases more than 10° C. upon annealing at 55° C.
8. A molding comprising P4HB produced by the processes of claim 1 .
9. A medical device produced by the process of claim 1 .
10. The device of claim 9 wherein the device is formed by machining the molding.
11. The device of claim 9 selected from the group consisting of suture anchors, screws, pins, including locking pins, bone plates, interference screws, tacks, nails, fasteners, rivets, staples, medullary cavity nails, clips, clamps, tubes, tissue engineering scaffolds, rotator cuff repair devices, meniscus repair devices, guided tissue repair/regeneration devices, articular cartilage repair devices, tendon repair devices, ligament repair devices, fixation devices for an implant, plastic surgery devices (including devices for fixation of facial and breast cosmetic and reconstructive devices), fixation devices for surgical meshes, facial reconstructive devices, spinal fusion devices, devices for treatment of osteoarthritis, imaging devices, and bone graft substitutes.
12. The device of claim 9 wherein the device further comprises a second polymer, nucleant, plasticizer, reinforcing element, bioactive agent, contrast agent, radiopaque marker and/or radioactive substance.
13. The device of claim 12 wherein the second polymer is a poly(lactide); poly(glycolide); poly(lactide-co-glycolide); poly(lactic acid); poly(glycolic acid); poly(lactic acid-co-glycolic acid); polycaprolactone; poly(orthoester); polyanhydride; poly(phosphazene); polyhydroxyalkanoates; poly-3-hydroxybutyrate; copolymer of 3-hydroxybutyrate with 3-hydroxyvalerate; P4HB copolymer; synthetically or biologically prepared polyester; polyester with one or more of the following monomeric units: glycolic, lactic; trimethylene carbonate, p-dioxanone, or ε-caprolactone; poly(lactide-co-caprolactone); polycarbonate; tyrosine polycarbonate; polyamide; synthetic or natural polyamide, polypeptide, poly(amino acid); polyesteramide; poly(dioxanone); poly(alkylene alkylate); polyether; polyethylene glycol; polyethylene oxide; polyvinyl pyrrolidone; polyurethane; polyetherester; polyacetal; polycyanoacrylate; poly(oxyethylene)/poly(oxypropylene) copolymer; polyacetal, polyketal; polyphosphate; phosphorous-containing polymer; polyphosphoester; polyalkylene oxalate; polyalkylene succinate; poly(maleic acid); chitin; chitosan; modified chitosan; hyaluronic acid and derivatives thereof; hydrophilic or water soluble polymer.
14. The device of claim 9 wherein the device is used for the repair, regeneration, or replacement of soft or hard tissues.