View Patent ↗The invention relates to a method for producing sandwich construction elements for substantially load-bearing and self-supporting building parts. In one embodiment of the invention, a method is provided including a) producing at least one layer of a mechanically bonded fiber nonwoven which is impregnated with a binder based on at least one heat-curable resin system b) curing the heat-curable resin system in order to produce at least one hardened layer of the fiber nonwoven, and fixed thermally, c) bringing a heat-foamable or heat-foamed phenol resin into contact with that surface of at least one hardened layer of the fiber nonwoven which has been modified according to step b), d) possibly annealing the composite produced in a) to c), and e) curing the further binder based on at least one heat-curable resin system.
1. A method for producing sandwich construction elements for essentially loadbearing and self-supporting parts of a building, said method comprising the steps of
a) producing one or more than one ply of a mechanically consolidated fibrous fleece based on naturally occurring raw materials selected from the group consisting of hemp, flax, jute, sisal, kenaf, cotton, wool, and mixtures thereof, each ply impregnated with a binder based on one or more than one heat-curable resin system,
b) curing the heat-curable resin system to produce one or more than one cured ply of the fibrous fleece, applying a surface structure to at least part of each ply of the fibrous fleece before and/or during curing; and/or applying and thermally fixing one or more than one further binder based on one or more than one heat-curable resin system to at least part of a surface of the cured ply of the fibrous fleece,
c) contacting a thermally foamable or foamed phenolic resin with the surface, as modified in step b), of one or more than one cured ply of the fibrous fleece,
d) optionally subjecting the composite produced under a) to c) to conditioning at temperatures in a range from 40 to 80° C., and
e) if applied, subjecting the further binder based on one or more than one heat-curable resin system and optionally applied in b) to curing in a range from 150 to 200° C., optionally under elevated pressure.
2. The method as claimed in claim 1 , wherein the applying the surface structure comprises placing a lattice, grid or structured tool on the ply as it cures.
3. The method as claimed in claim 2 , wherein the surface structure comprises angular, round, oval, honeycomb-shaped, dimplelike geometries.
4. The method of claim 1 wherein the binder used in step a) and/or b) is one or more than one heat-curable resin system based on phenolic, epoxy, amino and/or polyester resins.
5. The method of claim 1 wherein the contacting of the foamable phenolic resin with the cured ply in step c) is effected by foaming up the foamable phenolic resin applied to the surface of the cured ply.
6. The method of claim 1 wherein the contacting of foamed phenolic resin with the cured ply in step c) is effected by adhering the foamed phenolic resin to the cured ply.
7. The method-of claim 6 , wherein a structure is introduced onto a surface of the foamed phenolic resin by mechanical milling and/or a structured plate.
8. The method of claim 1 wherein reinforcing elements are introduced between the one or more than one cured ply of the fibrous fleece and the foamable or foamed phenolic resin.
9. The method of claim 8 wherein the reinforcing elements are selected from the group consisting of glass fibers, basalt fibers, plastic fibers, carbon fibers, unidirectionals, wovens, fleeces, and combinations thereof.
10. The method of claim 1 wherein reinforcing elements are introduced into the foamable or foamed phenolic resin during foam production.
11. The method of claim 10 , wherein the reinforcing elements have geometries selected from the group consisting of stripes, diamonds, cassettes or stars.
12. The method of claim 1 wherein the contacting of a thermally foamable phenolic resin with the surface of one or more than one cured ply further comprises forming recesses, in the one or more than one cured ply prior to the contacting.