Electrical circuit breaker
The invention relates to an electrical circuit breaker comprising an arc formation chamber and an arc extinguishing chamber, the arc formation chamber being at least partially bounded by a side flange or at least a part of a side wall consisting of a polymeric composition comprising a thermoplastic polymer, a triazine based flame retardant, at most 0-5 wt. % of phosphorous or halogen containing flame retardants, and 0-15 wt. % of a reinforcing agent, wherein thermoplastic polymer comprises a polyamide with a melting temperature of at least 260° C. and the triazine based flame retardant comprises at least 20 wt. % of melam, wherein the weight percentages (wt. %) are relative to the total weight of the polymeric composition.
1. An electrical circuit breaker comprising an arc formation chamber and an arc extinguishing chamber, the arc formation chamber being at least partially bounded by a side flange or at least a part of a side wall consisting of a polymeric composition comprising:
a thermoplastic polymer which comprises a polyamide with a melting temperature of at least 260° C.,
a triazine based flame retardant system comprising 70-100 wt. % of melam relative to the total weight of the flame retardant system, the flame retardant system being present in an amount such that the melam is present in an amount of at least 20 wt. % relative to the total weight of the polymeric composition,
at most 0-5 wt. % of phosphorous or halogen containing flame retardants, relative to the total weight of the polymeric composition, and
0-15 wt. % of a reinforcing agent, relative to the total weight of the polymeric composition.
2. The electric circuit breaker according to claim 1 , wherein the electric circuit breaker is a molded case circuits breaker (MCCB).
3. The electrical circuit breaker according to claim 1 , wherein the arc formation chamber comprises two side flanges consisting of individual plastic parts inserted in the arc formation chamber.
4. The electrical circuit breaker according to claim 1 , wherein melam is present in an amount of 20-40 wt. %, relative to the total weight of the polymeric composition.
5. The electrical circuit breaker according to claim 1 , wherein the polymeric composition consists of:
(a) 30-70 wt. % of a polyamide with a melting temperature of at least 260° C.,
(b) 20-40 wt. % of melam;
(c) 5-10 wt. % of fibrous reinforcement material;
(d) 0-40 wt. % of an inorganic filler; and
(e) 0-20 wt. % of other components; wherein
the weight percentages (wt. %) are relative to the total weight of the polymeric composition.
6. The electrical circuit breaker according to claim 1 , wherein melam is present in an amount of 30-40 wt. %, relative to the total weight of the polymeric composition.