Bimodal polyethylene composition for injection moulded articles
Bimodal high density polyethylene composition for producing molded articles comprising—an ethylene homopolymer or an ethylene alpha-olefin copolymer which is a bimodal high density polymer (COMPONENT A) in combination with—an alphanucleating agent (COMPONENT B),—a slip agent being a primary fatty acid amide, (COMPONENT C) and—one or more additives selected from antioxidants, acid scavengers, pigments and UV-stabilizers (COMPONENT D), the composition showing an increased the crystallization temperature and a decreased coefficient of friction compared to a bimodal HDPE composition prepared with the sole use of nucleating agent and compared to the sole use of a slip agent; and its use for producing injection molded articles, especially caps and closures.
1. Bimodal high density polyethylene composition for producing moulded articles comprising:
a) 92.6 to 99.4 wt % of the composition of a bimodal high density polymer comprising an ethylene homopolymer or an ethylene alpha-olefin copolymer (COMPONENT A) in combination with;
b) 0.5 to 2 wt % of the composition of talc, (COMPONENT B);
c) 0.05 to 0.4 wt % of the composition of a slip agent being behenamide, (COMPONENT C) and;
d) 0.05 to 5 wt % of the composition of one or more additives selected from antioxidants, acid scavengers, pigments and UV-stabilisers. (COMPONENT D).
2. High density polyethylene composition according to claim 1 , wherein Component A comprises:
(i) a low molecular weight ethylene homopolymer or copolymer and;
(ii) a high molecular weight ethylene homopolymer or copolymer.
3. High density polyethylene composition according to claim 2 , wherein the low molecular fraction (i) of Component (A) is an ethylene homopolymer with an MFR 2 in the range of 300 to 500 g/10 min and a density of more than 960 to 980 kg/m 3 and the high molecular weight fraction (ii) of Component (A) is an ethylene copolymer with an alpha-olefin comonomer selected from 1-butene or 1-hexene and wherein the weight ratio of fraction (i) to fraction (ii) is in the range of 40:60 to 60:40.
4. High density polyethylene composition according to claim 2 , wherein Component (A) is prepared in a two-step process comprising a first slurry polymerisation step for producing the low molecular weight fraction (i) and a second gas phase polymerisation step for producing the high molecular weight fraction (ii), wherein the second polymerisation step is carried out in the presence of the polymerisation product of the first step and wherein the first polymerisation step may be preceded by a prepolymerisation step.
5. High density polyethylene composition according to claim 1 , wherein Component D is an antioxidant and/or an acid scavenger.
6. High density polyethylene composition according to claim 1 , wherein Component (A) is a bimodal high density polymer composed of a low molecular weight ethylene homopolymer and a high molecular weight ethylene/1-butene copolymer and Component D is an antioxidant and/or an acid scavenger.
7. Injection moulded articles comprising the HDPE composition according to claim 1 .
8. The injection moulded article according to claim 7 , wherein the article is a cap or closure.
9. High density polyethylene composition according to claim 1 , wherein Component A has a molecular weight distribution of about 10 to about 35.