Process for manufacturing a metal part by selectively melting a powder
View Patent ↗A method of fabricating a metal part by selectively melting a powder, the method including: building up layer by layer on a plate and simultaneously with the part, at least one holder and support element for the part, the element being spaced apart and distinct from the part and being separated therefrom by a gap filled with non-melted powder; after the part has been made completely, removing at least some of the powder remaining in the gap between the part and the element, for example by suction, blowing, or vibration; and separating the part from the plate.
1. A method of fabricating a metal part by selectively melting a metal powder, the method comprising:
building up layer by layer on a plate and simultaneously with the part, at least one holder and support element for the part, the element being spaced apart from the part and being separated therefrom by a gap filled with non-melted powder;
after the part has been made completely, removing at least some of the powder remaining in the gap between the part and the element; and
separating the part from the plate wherein the distance between the at least one holder and support element and the part is determined using a chart, as a function of selected parameters, or a function of roughness of the part that is to be obtained.
2. A method according to claim 1 , wherein the support is spaced apart from the part by a distance lying in a range of 50 μm to 500 μm.
3. A method according to claim 1 , wherein the metal part, the at least one holder and support element, and the plate are subjected to heat treatment for releasing stresses before they are separated from one another.
4. A method according to claim 3 , wherein the heat treatment for releasing stresses includes heating the metal part, the at least one holder and support element, and the plate to a temperature lower than sintering temperature of the metal powder, for a determined duration.
5. A method according to claim 1 , wherein two holder and support elements are built up layer by layer together with the part on either side of the part, the two holder and support elements being spaced apart from the part and separated from the part by a gap filled with non-melted powder.
6. A method according to claim 1 , wherein the part and the at least one holder and support element are built up layer by layer by selectively melting the powder with help of a laser beam, the powder presenting mean grain size lying in a range of 10 μm to 50 μm, or with help of an electron beam, the powder presenting mean grain size lying in a range of 50 μm to 100 μm.
7. A method according to claim 1 , wherein the at least one holder and support element is hollow and includes stiffener means.
8. A method according to claim 1 , wherein the part is separated from the plate by cutting using an electro erosion wire.
9. A method according to claim 3 , wherein, during the heat treatment for releasing stresses, the metal part and the at least one holder and support element are kept in position relative to each other with help of at least one flange.
10. A method according to claim 1 , wherein, after the part has been separated from the plate, the part is subjected to a finishing treatment.